The stability of liquid ferrate(Ⅵ) produced by an innovative method was confirmed and the degradation characteristics of cyclic compounds(Benzene, Aniline, Toluene, 1,4-Dioxane) by liquid ferrate(Ⅵ) were investigated under the same reaction conditions. When it was compared with the ferrate manufactured by the wet oxidation method, the liquid ferrate was more stable. And the stability of liquid ferrate was tested at the storage temperature. As a result, only 17.7% of liquid ferrate(Ⅵ) has decomposed at the storage temperature(4˚C) for 28 days. Among the cyclic compounds, the aniline was rapidly degraded compare to other cyclic compounds, which seems to be due to the electron-donating ability of the substituent, -NH2 group. Especially, when 1,4-dioxane was compared with benzene, the decomposition rate of 1,4-dioxane was lower than that of benzene, suggesting that oxygen atoms hinder the electrophilic reaction. Among 4 cyclic compounds, it was observed that aniline has the highest rate constant than those of other cyclic compounds.

Ti-45at%AI-1.6at%Mn 조성을 갖는 금속간화합물의 장시간 및 반복산화 거동을조사하기 위하여 반응소결법 및 플라즈마 아크 용해법으로 제조한 시편에 대하여 800˚C에서는 반응소결재와 용제재 모두 등온 및 반복산화에 대하여 우수한 저항성을 나타내었다. 900˚C에서는 반응소결재의 경우에는 등온 및 반복산화에 대하여 우수한 저항성을 보였으며, 중량변화와 산화피막의 박리는 극히 적었다. 이에 비해 용제재의 경우에는 등온 및 반복산화에 의해 중향이 크게 변하였으며 피막의 박리도 극심하였다. 900˚C에 있어서 두 재료간의 이러한 산화거동 차이는 기지/산화물 계면 부근에 형성된 산화층의 차이에 기인하는 것으로 간주하였다. 반응소결재의 경우에는 계면 부근에 연속적인 AO3O3층이 형성되며, 이러한 층이 산화에 대한 보호막으로 작용하는데 비하여 용제재에 있어서는 계면 부근에 AO3O3와 TiO2의 혼합층이 형성되었다. 용제재의 반복산화시에 보여진 피막의 박리는 냉각시에 TiO2와 기지간의 열팽창계수 차이에 기인하여 발생하는 열응력을 TiO2가 견디지 못하고 박리를 초래한 것으로 해석하였다.