In the present study, the effects of electrodes type (copper, steel or CFRP) and design (plate or mesh) on electrical stability of conductive cement as exposed to various weathering conditions were investigated. To fabricate these composites, multiwalled carbon nanotube and carbon fiber were added to the cement composites by 0.6 and 0.4% by cement mass. Seven different types of electrodes were embedded to the samples, and their electrical stability was examined during the curing period. In addition, the fabricated samples were exposed to water ingress and cyclic heating conditions. Then, the compressive strength of the samples was evaluated to observe the interfacial bonding between the cement paste and electrodes. Based on the experimental results, it was found that the samples showed different electrical stability even their mix proportion was same. Thus, it can be concluded that the type and design of the electrodes are important in measuring the electrical properties of the conductive cement composites. Specifically, an improved electrical stability of electrodes is required when they are exposed to various weathering conditions.

본 연구는 EMG(electromyography) 텍스타일 전극 개발을 목적으로 레이어 수의 디자인 및 원단을 다르게 하여 성능 및 신호 획득 안정성을 평가한다. 레이징 및 프레스 공정을 통하여 텍스타일 전극을 제조하며 Layer-0, Layer-1, Layer-2로 레이어 유무 및 수에 따른 결과를 분석했다. 이에 레이어 유무에 따라서는 근활성 측정에 영향을, 수가 많을수록 높은 성능이 나타남을 확인할 수 있었다. Layer-2 구조로 통일하여 5가지의 원단(네오프렌, 스판덱스 쿠션, 폴리에스테르 100%, 나일론 스판덱스, 광목 캔버스)으로 전극을 제조해 실험해 보았다. 성능적인 면에서, 원단의 중 량이 높은 나일론 스판덱스가 높은 성능을 보였으며, 스판쿠션 텍스타일 전극이 근활성도 수득에 높은 안정성을 보 였다. 이에 위 연구는 레이어에 따른 성능 연관성과 전극-피부사이의 닿는 면적 간의 관계 등을 고찰하여 슬리브 전체의 의복압을 늘리는 대신 특정 센서 측정 부위에만 높은 압력을 가함으로 차후 연구에서 레이어의 수 및 물성에 따른 전극의 공학적 설계 가능성을 제시한 의의가 있다.