As the demand for appropriate heat dissipation measures to improve product stability and performance continues to increase and product design becomes highly integrated, research to improve heat transfer performance while maintaining the same area or size is required. In this study, the sample-shaped aluminum plate was treated as upper-coating, and the thickness of the coating was divided into 1mm, 2mm, and 3mm, respectively, and the coating material was applied with silver, copper, and graphene. The temperature condition of the heat source was set to 473K, and heat dissipation analysis was performed under natural convection. The thermal performance was compared and analyzed through temperature distribution, flow velocity distribution, and heat flux, and it was confirmed that the high thermal conductivity of graphene compared to other materials had a dominant effect on the increase in the conduction heat transfer rate. And it was confirmed that the high surface temperature of the graphene coating also increased the heat transfer rate by convection, thereby enhancing the heat dissipation effect.

In this study, a method to remove residual powder on a multi-layered graphene and a new approach to transfer multi-layered graphene at once are studied. A graphene one-step transfer (GOST) method is conducted to minimize the residual powder comparison with a layer-by-layer transfer. Furthermore, a residual powder removing process is investigated to remove residual powder at the top of a multi-layered graphene. After residual powder is removed, the sheet resistance of graphene is decreased from 393 to 340 Ohm/sq in a four-layered graphene. In addition, transmittance slightly increases after residual powder is removed from the top of the multi-layered graphene. Optical and atomic-force microscopy images are used to analyze the graphene surface, and the Ra value is reduced from 5.2 to 3.7 nm following residual powder removal. Therefore, GOST and residual powder removal resolve the limited application of graphene electrodes due to residual powder.

For the automotive application, graphene-glass composites were fabricated using E-glass fiber(GF) coated with various types of graphene nanosheets deposited by electrophoretic deposition. Graphene oxide(GO) was first synthesized using a modified Hummer’s method and its subsequent ultrasonic treatment in deionized water produced a stable stop of the GO. Glass fiber was immersed in water and GO suspension near the copper anode. The potential applied between the electrodes caused the GO to move toward the anode. In addition, the GO coated yarn was exposed to hydrazine hydrate at 100℃ to obtain a reduced graphene oxide(rGO) coating yarn. Both GO and rGO coated glass fiber yarns were used to fabricate unidirectional epoxy-based multi-scale composites by passive lay-up. The presence of a conductive rGO coating on glass fiber improves both the electrical conductivity and thermal conductivity of the composite. In addition, rGO-based epoxy-glass composites have been used to improve the dielectric constant, providing the option of using this structure for electromagnetic interference shielding.

This study presents the fatigue life analysis of a graphene-reinforced steel pipe. For the analysis, ANSYS was used, and the analysis results were compared with a normal steel pipe. From the analysis, it is shown that the graphene-reinforced steel pipe gives the fatigue life of 101,300 cycles, which is 11 times more than that of the normal steel pipe.