Various silanes, amino silane, vinyl silane, sulfur silane (TESPD), and ZS (TESPD/zinc soap complex), are added into chlorinated isobutylene-isoprene copolymer (CIIR)/soft clay/carbon black (CB) and CIIR/hard clay/CB compounds and they are investigated with respect to the vulcanization characteristics, the processability, and the mechanical properties. Comparing hard clay and soft clay filled compounds, hard clay (Suprex) filled system shows a higher die C tear than the soft clay (GK) filled one. The other properties (Mooney, extrusion torque/pressure, torque rise (MH-ML), modulus at 300%) are close to each other. Among various silanes, the ZS treated hard clay (Suprex) compound shows the highest mechanical property following hard clay(S)/vinyl silane(V) and soft clay(GK)/vinyl silane(V) compounds. The TESPD and the ZS effectively helps a formation of a strong 3-dimensional network structure between silica and CIIR via coupling reaction due to bifunctional nature of TESPD. In addition to that, the ZS added compounds show both a better processability and mechanical properties compared to the S2 ones at low concentration due to improved compatibility between zinc soap and CIIR matrix. Only the ZS added compound shows both improved processabilities (Mooney, Extrusion torque-& pressure) and improved mechanical properties (degree of crosslinking, elongation modulus, tear, and fatigue to failure counts) on both CIIR/hard clay/CB and CIIR/soft clay/CB compounds.

UO2분말에 PVA-Al(III) 착물과 AlOOH를 각각 0.03~1.0wt%를 첨가하여 소결체를 제조한 후 소결체 특성을 비교하였다. PVA-Al(III) 착물과 AlOOH는 1000˚C의 소소분위기에서 열분해하는 경우 생성상은 θ-Al2O3이었다. 순수 UO2분말에 비해 AlOOH가 첨가된 혼합 분말의 곁보기 밀도는 더 높았고, PVA-Al(III) 착물이 첨가된 혼합 분말은 더 낮은 겉보기 밀도를 보였다. AlOOH가 첨가된 소결체의 경우 약 800˚C 부근에서 치밀화가 시작되었지만, PVA-Al(III) 착물이 첨가된 소결체의 경우에는 약 900˚C에서 치밀화가 시작되었다. 기공 크기 분포는 AlOOH가 첨가된 UO2소결체의 경우에 monomodal 형태로, 그리고 PVA-Al(III) 착물의 첨가된 소결체의 경우에는 bimodal 형태로 나타났다. 결정립 크기는 1wt% 첨가시 AlOOH가 첨가된 UO2소결체의 경우에 약 13μm이었지만, PVA-Al(III) 착물의 첨가된 소결체의 경우에는 약 36mum까지 성장하는 현저한 효과를 확인하였다.