In this study, the experiments and analyses were carried out in order to investigate the fracture characteristics on the adhesive at the specimen bonded with aluminum and aluminum-foam. The same conditions were given for the experiments and analyses. The results are investigated by the graph of reaction force according to displacement. It was found that the experimental and the analytical data were very similar to each other. On the basis of the data, the reliability of the analysis data could be confirmed. The notches were produced at the distances of 40, 110, 150, and 190 mm from the front of the test specimen, and the maximum reaction force was compared accordingly. It was found that the highest reaction force was generated at the front end of the adhesive and the lowest reaction force was found at the middle of the adhesive interface. Finally, when the equivalent stress in the test specimen was examined, it was found that the highest stress was obtained at the distance of 110 mm. It can be deduced. As the notch formation point are similar to the point when stress is dispersed as the adhesive is peeled off, it is possible to infer the high stress compared to other test specimens.

In this study, we investigated the properties of adhesive materials with different lightweight materials such as CFRP and Al-foam. The specimens were tested and analyzed using DCB (Double Cantilever Beam) specimens. In order to secure the reliability of the finite element method, the test and analysis were carried out, and the reliability of the finite element method was secured by using the graph of reaction force to displacement based on the experiment and analysis. The study on the adhesive failure characteristics according to the position of notch hole proceeded. Notch holes were generated at the locations of 40, 110, 150 and 190 mm from the beginning of the specimen near the bonding interface, and the analysis conditions used were the same as those used for securing reliability. The obtained study results are compared with reaction force and equivalent stress. In the case of reaction force, the overall tendency is similar but the difference in maximum reaction force is found. It was found that higher reaction forces appeared at the beginning than at the end of the bonding interface. When the equivalent stresses in the specimens were examined, the value of CFRP was seen to be 30 times higher as much as that of Al-foam.