PURPOSES : The increase in particulate matter due to increased air pollutant emissions has become a significant social issue. According to the Ministry of Environment, air pollutants emitted from large-scale businesses in 2022 increased by 12.2% compared to the previous year, indicating that air pollution is accelerating owing to excessive industrialization. In this study, TiO2, which is used to reduce airborne particulate, was used. The TiO2 coating fixation and dynamic pressure coating-type TiO2 fixation methods were used to solve the material peeling phenomenon caused by gravity, which is a limitation when the TiO2 penetration method is applied to a vertical concrete structure along the road. The long-term durability and performance were analyzed through environmental resistance and NOx removal efficiency evaluation experiments. These analyses were then assessed by comparing the NOx removal efficiency with the dynamic pressure permeationtype TiO2 fixation method used in previous studies. METHODS : To evaluate the long-term durability and performance of the TiO2 coating fixation method and dynamic pressure coating TiO2 fixation method for vertical concrete structures, specimens were manufactured based on roadside vertical concrete structures. Environmental resistance tests such as the surface peeling resistance test (ASTM C 672) and freeze-thaw resistance test (KS F 2456) were conducted to evaluate the long-term durability. To evaluate the long-term performance, the NOx removal efficiency of TiO2 concrete owing to road surface deterioration during the environmental resistance test was evaluated using the NOx removal efficiency evaluation equipment based on the ISO 22197-1 standard. This evaluation was compared and analyzed using the dynamic pressure infiltration TiO2 fixation method. RESULTS : The long-term durability of the TiO2 coating fixation and dynamic pressure coating TiO2 fixation methods were evaluated using environmental resistance tests. During the surface peeling resistance test, the TiO2 material degraded and partially detached from the concrete. However, the NOx removal efficiency was ensured by the non-deteriorated and fixed TiO2 material. The long-term performance was confirmed through a freeze-thaw resistance test to evaluate the NOx removal efficiency after 300 cycles of surface deterioration. The results showed that when the TiO2 coating fixation and dynamic pressure infiltration TiO2 fixation methods were applied to vertical concrete structures, the durability of the structure was not compromised. In comparison to the dynamic pressure infiltration TiO2 fixation method, the NOx removal efficiency observed during the surface peeling resistance test was lower, while the freeze-thaw test exhibited notably higher removal efficiency. CONCLUSIONS : To solve the material peeling phenomenon caused by gravity, the long-term durability and performance were evaluated by applying the TiO2 coating fixation and dynamic pressurized coating TiO2 fixation methods to vertical concrete specimens. Long-term durability was confirmed through environmental resistance tests, and long-term utility was secured by measuring the NOx removal efficiency according to surface degradation. These findings show that implementing the TiO2 coating fixation method and dynamic pressure coating TiO2 fixation methods on-site effectively reduce NOx.

PURPOSES : Advancements in science and technology caused by industrialization have led to an increase in particulate matter emissions and, consequently, severity of air pollution. Nitrogen oxide (NOx), which accounts for 58% of road transport pollutants, adversely affects both human health and the environment. A test-bed was constructed to determine NOx removal efficiency at the roadside. TiO2, a material used to reduce particulate matter, was used to remove NOx. It was applied to a vertical concrete structure using the dynamic pressurized penetration TiO2 fixation method, which can be easily applied to vertical concrete structures. This study was conducted to evaluate the NOx removal efficiency of the dynamic pressurized-penetration TiO2 fixation method in a test-bed under real roadside conditions. METHODS : A test-bed was constructed in order to determine the NOx removal efficiency using the dynamic pressurized penetration TiO2 fixation method on the roadside. The dynamic pressurized-penetration TiO2 fixation method was applied by installing a vertical concrete structure. NOx was injected into the test-bed using an exhaust gas generator. By installing a shading screen, the photocatalytic reaction of TiO2 was suppressed to a maximum concentration of 1000 ppb along the roadside. The removal efficiency was evaluated by measuring NOx concentrations. In addition, illuminance was measured using an illuminance meter. RESULTS : From the results of the analysis of the NOx removal efficiency in the test-bed which the dynamic pressurized type TiO2 fixation method was applied to, an average removal efficiency ranging from 18% to 40% was achieved, depending on the illuminance. Similarly, according to the results of the evaluation of the NO removal efficiency, an average of removal efficiency ranging from 20% to 62% was achieved. Thus, the NOx removal efficiency increased when the illuminance was high. CONCLUSIONS : From the results of the experiment conducted, the efficiency of NOx removal per unit volume was obtained according to the illuminance of TiO2 concrete along an actual road. Field applicability of the dynamic pressurized-penetration-type TiO2 fixation method to vertical concrete structures along roads was confirmed.

PURPOSES : Recently, air pollution caused by particulate matter has been worsening. Among the substances generating particulate matter, NOx is the main precursor of particulate matter and is widely distributed in areas with a high volume of traffic. TiO2 has been used as a material for removing NOx through a chemical reaction as a photocatalyst. In this context, the reduction of NOx through TiO2 concrete is proposed. However, the research on the surface deterioration on the performance of TiO2 concrete is not documented yet. Therefore, the objective of this study was to evaluate the long-term durability and NOx removal efficiency of TiO2 concrete by considering the concrete surface deterioration. METHODS : Freezing–thawing resistance test (KS F 2456) and scaling test (ASTM C 672) were performed to investigate the variation in the TiO2 penetration distribution and NOx removal efficiency of TiO2 concrete corresponding to surface deterioration. The long-term durability of TiO2 concrete was evaluated through an environmental resistance test and changes in TiO2 penetration depth and distribution characteristics. In addition, the NOx removal efficiency of TiO2 concrete was evaluated as surface deterioration occurs. RESULTS : As a result of the freeze–thawing resistance test, a relative dynamic elastic modulus of more than 80 % was detected. In addition, a TiO2 penetration depth of 0.3 mm, NOx removal efficiency of 11.2 %, and a 30 % of TiO2 surface prediction mass ratio were achieved after 300 cycles. As a result of visual observation of the scaling test, “0, no scaling” was secured. After 50 cycles of scaling test, the TiO2 penetration depth, NOx removal efficiency, and TiO2 surface prediction mass ratio were 0.3 mm, 36.3 %, and 63 %, respectively. Through the results of the environmental resistance test, the excellent long-term durability and NOx removal efficiency of TiO2 concrete were confirmed. CONCLUSIONS : As a result of the experiment, long-term durability and NOx removal efficiency of TiO2 concrete were secured. The application of TiO2 concrete can be a good alternative with long-term performance and durability.

PURPOSES : NOx is a particle matter precursor that is harmful to humans. Various methods of removing NOx from the air have been developed. TiO2 and activated carbon are particularly useful materials for removing NOx, and the method is known as particulate matter precursor reduction. The removal of NOx using TiO2 requires sunlight for the photocatalytic reaction, whereas activated carbon absorbs NOx particles into its pores after contact with the atmosphere. The purpose of this study is to evaluate the NOx removal efficiency of TiO2 and activated carbon applied to concrete surfaces using the penetration method. METHODS : Surface penetration agents, such as silane-siloxane and silicate, were used. Photocatalyst TiO2 and adsorbent activated carbons were selected as the materials for NOx removal. TiO2 used in this study was formed by crystal structures of anatase and rutile, and plant-type and coal-type materials were used for the activated carbon. Each surface penetration agent was mixed with each particulate matter sealer at a concentration ratio of 8:2, and the mixtures were sprayed onto the surface. The NOx removal efficiency was evaluated using NOx removal efficiency equipment fabricated in compliance with the ISO 22197-1 standard. RESULTS : Anatase TiO2 showed a maximum NOx removal efficiency of 48% when 500 g/m² was applied. However, 500 g/m² of rutile TiO2 showed a NOx removal efficiency of up to 10%. When 700 g/m² of coal-based activated carbon and plant-based activated carbon was used, NOx removal efficiencies of up to 11% and 14%, respectively, were obtained. CONCLUSIONS : Rutile TiO2, a coal-based activated carbon, and plant-based activated carbon have lower NOx removal efficiencies than anatase TiO2. A lower amount of anatase TiO2 (500 g/m²), compared to the other spraying volumes, yielded the most significant NOx removal efficiency under optimal conditions. Therefore, it is recommended that 500 g/m² of anatase TiO2 should be sprayed onto concrete structures to improve the economic and long-term performance of these structures.

PURPOSES: In areas of high traffic volume, such as expressway across large cities, the amount of nitrogen oxides (NOx) emitted into the atmosphere as air pollution can be significant since NOx gases are the major cause of smog and acid rain. Recently, the importance of NOx removal has arisen in the world. Titanium dioxide (TiO2), that is one of photocatalytic reaction material, is very efficient for removing NOx. The NOx removing mechanism of TiO2 is the reaction of solar photocatalysis. Therefore, TiO2 in road structure concrete need to be contacted with ultraviolet rays (UV) to be activated. In general, TiO2 concretes are produced by replacement of TiO2 as a part of concrete binder. However, considerable portion of TiO2 in concrete cannot contact with the pollutant in the air and UV. Therefore, TiO2 penetration method using the surface penetration agents is attempted as an alternative in order to locate TiO2 to the surface of concrete structure. METHODS: This study aimed to evaluate the NOx removal efficiency of photocatalytic concrete due to various TiO2 application method such as mix with TiO2, surface spray(TiO2 penetration method) on hardened concrete and fresh concrete using surface penetration agents. The NOx removal efficiency of TiO2 concrete was confirmed by NOx Analyzing System based on the specification of ISO 22197-1. RESULTS: The NOx removal efficiency of mix with TiO2 increased from 11 to 25% with increasing of replacement ratio from 3 to 7%. In case of surface spray on hardened concrete, the NOx removal efficiency was about 50% due to application amount of TiO2 with surface penetration agents as 300, 500 and 700g/m2. The NOx removal efficiency of surface spray on fresh concrete due to all experimental conditions, on the other hand, which was very low within 10%. CONCLUSIONS: It was known that the TiO2 penetration method as surface spray on hardened concrete was a good alternative in order to remove the NOx gases for concrete road structures.

The objective of this research was to test whether, under controlled laboratory conditions, hybrid SNCR/SCR process improves NOx removal efficiency in comparison with the SNCR only. The hybrid process is a combination of a redesigned existing SNCR with a new downstream SCR. NOx reduction experiments using a hybrid SNCR/SCR process have been conducted in simple NO/NH3/O2 gas mixtures. Total gas flow rate was kept constant 4 liter/min throughout the SNCR and SCR reactors, where initial NOx concentration was 500 ppm in the presence of 5% or 15% O2. Commercial catalysts, V2O5-WO3-SO4/TiO2, were used for SCR NOx reduction. The residence time and space velocity were around 1.67 seconds and 2,400 h-1 or 6000 h-1 in SNCR and SCR reactors, respectively. NOx reduction of the hybrid system was always higher than could be achieved by SNCR alone at a given value of NH3SLIP. Optimization of the hybrid system performance requires maximizing NOx removal in the SNCR process. An analysis based on the hybrid system performance in this lab-scale work indicates that a equipment with NOxi=500 ppm will achieve a total NOx removal of about 90 percent with NH3SLIP ≤ 5 ppm only if the SNCR NOx reduction is at least 60 percent. A hybrid SNCR/SCR process has shown about 26～37% more NOx reduction than a SNCR unit process in which a lower temperature of 850℃ turned out to be more effective.