Preparation of activated carbon from biomass residue with conventional steam activation was conducted to find the alternative raw materials for meeting the high demand for low-cost porous material in the desiccant application. In this study, activated carbons were produced from dead camphor leaves using two-step methods at different preparation temperatures. The characterization results revealed that the prepared activated carbons have a surface area of 700 m2/g, with 75% of microporosity. The water vapor sorption study reported that the water uptake of camphor leaf-based activated carbons was strongly affected by the pore properties of the materials. Moreover, from the water adsorption kinetics, it was observed that the rate constant of adsorption was varied at each relative pressure, which can be assumed that the water adsorption mechanism is different at each relative pressure. From these results, it was revealed that the prepared camphor leaf-based activated carbons have a promising ability to adsorb water vapor from humid air.

Granular Activated Carbon (GAC) has been proven to be an excellent material for many industrial applications. A systematic study has been carried out of the kinetics of physical as well as chemical activation of phenolic resin chars. Physical activation was carried out using CO2 and chemical activation using KOH as activating agent. There are number of factors which influence the rate of activation. The activation temperature and residence time at HTT varied in the range 550~1000℃ and ½~8 hrs respectively. Kinetic studies show that the rate of chemical activation is 10 times faster than physical activation even at much lower temperature. Above study show that the chemical activation process is suitable to prepare granular activated carbon with very high surface area i.e. 2895 m2/g in short duration of time i.e. 1 to 2 hrs at lower temperature i.e. 750℃ from phenolic resins.