Using microwave synthesized HAp nano powder and polymethyl methacrylate (PMMA) as a pore-forming agent, the porous biphasic calcium phosphate (BCP) ceramics were fabricated depending on the sintering temperature. The synthesized HAp powders was about 70-90 nm in diameter. In the porous sintered bodies, the pores having were homogeneously dispersed in the BCP matrix. Some amounts of pores interconnected due the necking of PMMA powders which will increase the osteoconductivity and ingrowth of bone-tissues while using as a bone substrate. As the sintering temperature increased, the relative density increased and showed the maximum value of 79.6%. From the SBF experiment, the maximum resorption of ion was observed in the sample sintered at .

Silica hydrogel was synthesized by the reaction of liquid sodium silicate with sulfuric acid. The condensation polymerization of the synthesized hydrogel was carried out via an aging process under the acidic or alkaline conditions. Nano porous silica with the pore size below 3 nm and surface area of , was obtained by the above processes in acidic ranges(pH : 3~5). The pore size and surface area of the silica varied with pH, and in alkaline ranges(pH : 8~10), those were 21 nm and respectively. The characteristics of the silica varied with the thermal treatment which caused the change of surface area, pore volume and pore diameter.