Sintered steels are materials characterized by residual porosity, whose dimension and morphology strongly affect the fatigue crack growth behaviour of the material. Prismatic specimens were pressed at from Astaloy CrM powder and sintered varying the sintering temperature and the cooling rate. Optical observations allowed to evaluate the dimensions and the morphology of the porosity and the microstructural characteristics. Fatigue tests were performed to investigate the threshold zone and to calculate the Paris law. Moreover tests were performed to complete the investigation. Both on fatigue and samples a fractographic analysis was carried out to investigate the crack path and the fracture surface features. The results show that the Paris law crack growth exponent is around 6.0 for sintered and around 4.7 for sintered materials. The same dependence to process parameters is not found for .

본 연구는 균열이 발생한 R/C보를 탄소섬유시트(Carbon fiber sheet)로 보수했을 경우 시트의 박락과 균열의 확대 및 성장 메커니즘을 조사한 것이다. 실험변수는 하중형식, 재하속도, 사전균열 유무 등이다. 실험에서, 보의 파괴는 전단력 급변에 의한 재하점 직하부의 단차박리의 발전과 전파로 시작됨이 확인되었지만, 파괴기구는 하중형식, 재하속도, 사전균열 유무 등에 영향을 받지 않았다. 특히, 사전균열을 갖는 보의 경우, 균열의 성장은 재하점 직하의 특정한 균열에 집중되고, 이 균열의 확장에 의한 탈착이 보의 파괴를 이끌었다.