In this work, the sulfonic acid group was introduced into the resorcinol–formaldehyde (RF) microspheres by the addition of p-phenolsulfonic acid during the polycondensation process of RF. The hydrophilicity of the sulfonated RF allowed KOH to infiltrate inside the microspheres, which enhanced the formation of mesopores in the carbon microspheres during the activation process by KOH. SEM and TEM observations and N2 adsorption measurements verified the formation of abundant mesopores in the porous carbon microspheres. The BET surface area of these mesoporous carbons exceeded 2000 m2/ g. In 17 m NaClO4 “water-in-salt” (WIS) electrolyte-based supercapacitor, the synthesized mesoporous carbon exhibited high specific capacitance of 170 F/g at current density of 0.5 A/g, comparable to those in regular KOH electrolyte. When graphite was used as current collectors, the symmetric cell could operate at 2.5 V, and the mesoporous carbon exhibited an energy density of 43 Wh/kg at power density of 0.25 kW/kg, and 25 Wh/kg at power density of 6.25 kW/kg, respectively, which were superior to those using Pt or stainless steel as current collectors. The mesoporous carbon/graphite was an excellent electrode in new-generation “WIS” electrolyte-based high-voltage supercapacitor due to their high energy and power density.

The present work is aimed at evaluating the kinetics and dynamic adsorption of methylene blue by CO2- activated carbon gels. The carbon gels were characterized by textural properties, thermal degradation and surface chemistry. The result shows that the carbon gels are highly microporous with surface area of 514 m2/g and 745 m2/g for resorcinol-to-catalyst ratios of 1000 (AC1) and 2000 (AC2), respectively. The kinetics data could be described by pseudo-first-order model, with a longer duration to attain equilibrium due to restricted pore diffusion as concentration increases. Also, AC1 exhibits insignificant kinetics with fluctuating adsorption with time at concentrations of 20 and 25 mg/L. However, AC1 reveals a better performance than AC2 in dynamic adsorption due to concentration gradient for molecules diffusion to active sites. The applicability of Yoon–Nelson and Thomas models indicates that the dynamic adsorption is controlled by external and internal diffusion.

Kevlar was chemically surface modified with resorcinol-formaldehyde(RF) prepolymer and VP rubber latex for application to high strength tirecords. RF prepolymer was easily obtained by polymerization at room temperature in the presence of a base catalyst. The mechanical and thermal properties of Kevlar were not significantly changed during surface treated under various conditions. The change of adhesion with rubber were investigated through H-test method. Maximum increase of adhesion force between rubber and Kevlar was obtained up to 40% than that of untreated one when the fiber was soaked in RFL dipping solution and thermally treated at 170℃ for 3 - 5min.

본 연구에서는 resorcinol과 formaldehyde를 이요하여 수상에서 축중합시켜 겔을 만든 후 저온 초임계 건조 공정을 이용하여 겔 구조의 변형없이 용매를 제거하여 내무 표면적과 같은 에어로겔의 최종 물성에 미치는 영향을 알아보기 위하여 고형분의 농도(2-5%)를 변화시켜 실험한 결과 초기 반응조건이 반응시간 및 최종물성에 변수가 됨을 알 수 있었다. 또한 제조된 에어로겔에 100-300˚C까지 온도를 가하며 표면 특성을 분석한 결과 열을 가함에 따라 기공의 크기가 커지고 표면적이 감소됨을 관찰할 수 있었다.