Hydroxyapatite (HA) is well known as a biocompatible and bioactive material. HA has been practically applied as bone graft materials in a range of medical and dental fields. In this study, two types of dense hydroxyapatite ceramics were prepared from natural bones and synthetic materials. The biocompatibility of HA ceramics for supporting osteoblast cell growth and cytotoxicity using an in vitro MG-63 cell line model were respectively evaluated. Artificial hydroxyapatite shows relative density of 93% with 1-2 μm after sintering, but a hydroxyapatite compact derived from bovine bone has low sintered density of 85% with a small content of MgO. Irrespective of the starting raw materials, both types of sintered hydroxyapatite displayed similar biocompatibility in the tests. FE-SEM observations showed that most MG-63 cells had a stellar shape and formed an intercellular matrix containing fibers on sintered HA. The cells were well attached and grown over the HA surface, indicating that there was no toxicity.

본 연구에서는 지하 콘크리트 구조물의 누수 균열에 사용되는 주입형 누수보수재료의 품질관리 방안으로 규격화된 국제표준 ISO TS 16774, Part 2 Test method for chemical resistance를 이용하여 현재 우리나라 누수보수현장에서 사용하고 있는 주입형 누수보수재료 2계열 (합성고무계, 시멘트계), 3종류 씩, 총 9 종류의 보수재료에 대한 지하 콘크리트 구조물이 처한 화학적 환경의 저항 안정성을 연구·검토하였다. 그 결과, 합성고무계는 RG-3를 제외하고, 산에 대한 저항력을 높일 수 있는 재료적 검토가 필요하고, 시멘트계는 수산화나트륨, 염화나트륨에 대한 저항을 높일 수 있는 재료적 검토의 필요성이 확인되었다. 이러한 결과는 콘크리트 구조물의 화학적 환경에서의 보수재료 선정 시 기본 지 표로 사용가능 할 것으로 판단된다. 또한, 추후에 연구 개발 되는 보수재료의 품질 향상에 반영할 수 있는 기준 자료의 활용을 기대할 수 있다.