Materials design and processing development proposed in this study, aims at contributing to high wear resistant and friction characteristics. To find wear resistant and friction with inner elbow pipe, it is needed hardness and frictional condition test to be capable of supplying with high Cr casting steel. The result of HTV(heat treatment in vacuum) shows that hardness increased with increasing Cr content in % carbide phase. It was about 7∼10% of hardness improvement compared to original casting elbow pipe. This behavior of the hardness of Cr casting steel was explained by the types of chemical bonds that hold atoms together in Cr carbide phase. Through the friction coefficient and wear loss test, with the increasing of Cr wt% reduction in the coefficient of friction and wear loss.

도로표지용 도료의 품질기준은 KS M 6080의 품질기준을 만족하는 제품들의 경우에도 시공 후 일정기간이 경과한 후에는 도료 자체의 부착력 문제로 교통량 증가에 따른 자동차 차륜에 의한 도료 자체의 마모 손실에 의하여 재귀반사 기능을 부여하는 유리알의 마모 및 탈리로 시인성이 급격히 저하되고 있다. 이에 따른 야간 교통 사고율 증가와 동시에 추가 교통 안전을 위한 부가 보완시공으로 안전시설 제비용이 직접비용으로 유발되고 있으며, 직접비용보다 추가공사로 인한 교통체증으로 사회간접 비용이 증가되고 있다. 특히, 차선의 품질 규격이 KS M 6080 제품에 만족한다 하더라도 빗물의 수막(水膜)에 의한 유리알의 굴절율 차로 재귀반사기능을 하는 차선 도료용 유리알의 기능을 발휘하지 못하여 운전자의 시인성은 열악함을 알 수 있다. 따라서, 국외에서 많이 사용되고 있는 마모성이 우수한 수용성 차선도료, 고성능 융착식 도료, 상온경화형 도료를 도입하여 성능을 비교 검토하였다. 본 연구에서는 차선재료의 내구성 향상을 위해 EN 1436규격에 의한 내마모성 시험을 수용성, 융착식, 상온경화형 도료에 실시하여, 재귀반사도 성능이 우수한 차선재료의 적용 가능성을 확인하였다.

To meet the demands for use in extremely abrasive and corrosive environments, a new material was developed. The VeKo25Cr distinguishes itself through specifically selected amounts of carbon and carbide forming elements such as Cr, Mo, V, W and Nb. The alloy is based on a Fe matrix. The strength after heat treatment and the wear and corrosion properties are compared to those of other materials. VeKo25Cr can be combined with easy-to-process materials such that the difficult handling is minimized to those places on the piece most subjected to operational wear.

Laser Powder Deposition (LPD) is a technology capable of modifying a metallic structure by adding the appropriate material to perform a desired function. LPD offers a unique fabrication technique that allows the use of soft (tough) materials as base structures. Through LPD a hard material can be applied to the base material with little thermal input (minimal dilution and heat-affected-zone {HAZ}), thus providing the function of a heat treatment or other surface modifications. These surface modifications have been evaluated through standard wear testing (ASTM G-65), surface hardness (Rc), micro-hardness (vickers), and optical microscopy.

Conventional high-speed steels, which are carbide decentralized materials, are used for sliding parts, but they lack sufficient hardness for some applications. Improvement of surface hardness is possible for high-Cr steels through nitriding. However, nitriding P/M parts is not advisable without sealing the porosity before treatment, as they will become brittle. However, it is difficult to seal the pores with steam treatment, because high-Cr steel has a passive film on the surface. Controlling nitriding by decreasing the amount of oxygen on the surface to be nitrided, and grinding to decrease the porosity of the surface, makes it possible to produce a material that has reasonable and sufficient hardness in the required areas.

Thermal spray coating process has proven to be effective at producing hard, dense, wear resistance coatings on the relatively mild substrates. Among several spraying techniques, HVOF (High Velocity Oxygen Fuel) and plasma coating processes, which are preferentially used for the wear resistance application such as capstans, have been applied in this study. The effects of pre-treatment, it-process and post-treatment parameters on the wear and mechanical properties of WC+12%Co, Cr3C2 and Al2O3 powder coatings have been investigated and correlated with the microstructures. The results indicated that the carbide coating was more preferable to the oxide coatings and the post-treatments consisting of vacuum annealing and sealing on carbide coatings led to significant improvements in wear resistance, adhesive strength and coating phase stabilization over the other processing techniques in this application.

When a commercial prealloyed Fe-powder(Fe-5Cr-lMo-2Cu-0.5P-3C) is liquid phase sintered at 116, liquid precipitates with various shapes form within solid grains during the initial stage of sintering. The shape of a liquid precipitate changes pith the increment of their size from sphere(with radius<0.3), a transient polyhedron with more than 7 faces(1~2 ), cuboid(3~5 ), and finally to sphere(>5 ). The shapes of liquid precipitates closely resemble the growth shapes predicted on the basis of solid-liquid interfacial energy and the coherency strain energy with anisotropic elastic constants in the diffusion zone around the precipitates.