The size of crystallites in mono-dispersed cubic silver bromide grains was measured by applying a powder X-ray diffraction method and Scherrer's equation to grains that were suspended in swollen gelatin layers. In order to evaluate the existence of defects, the measured crystallite size was compared to those measured by using a scanning electron microscope. In the case of the grains prepared by the controlled double jet method, the size of crystallites was equal to the edge length of the grains that had edge lengths smaller than 400 nm. This result proved the usefulness of the above-stated method for measuring the size of crystallites and also evaluating the presence of any crystal defect in each grain. In the case of the grains, which were precipitated in the presence of a sensitizing dye and potassium iodide, the size of crystallites was smaller than the edge's length, indicating the discontinuities in the grains introduced during the precipitation process.

σ-VFe 금속간화합물에 대한 기계적 합금화(MA) 효과를 중성자 및 X선 회절법으로 조사하였다. MA 분말의 구조분석은 X선 회절(Cu-Kα) 린 중성자회절(HRPD, λ=1.835Å)을 이용하여 행하였다. σ-VFe화합물의 MA시 큰 구조변화가 관찰되었으며, MA 60시간의 경우 Fe-Fe 훤자분포는 unit cell에 30개의 원자를 포함하고 있는 σ상의 tetragonal구조에서 120˚C이상에서 안정하게 존재하는 α-(V,Fe) 고용체의 bcc 구조로 상변화함을 알 수 있었다. 또한 α-VFe 화합물에 대한 중성자 및 X선 회절패턴의 비교분석을 행하였으며 그 결과 σ상이 가지는 화학적 규칙성에 기인하는 (101)과 (111) 회절 피크가 중성자 회절에서 뚜렷하게 관찰됨을 알 수 있었다.