Nowadays, transferred type arc plasma torches have been widely present in industrial applications, in particular, using melting pool of electrically conducting materials such as arc furnace, welding and volume reduction of radioactive wastes. In these applications, the melting pools are normally employed as an anode, thus, heat flux distributions on anode melting pool need to be characterized for optimum design of melting pool system. For this purpose, we revisited the one-dimensional model of the anode boundary layer of arcs and solved governing equations numerically by using Runge-Kutta method. In addition, the direct melting process of non-combustible wastes in the crucibles were discussed with the calculation results.

Present study investigated the waste form integrity of melted products generated from PAM-MSO system, which is proposed and developed to compensate the drawbacks of each system. The disposal suitability of the melting solidification products generated from the plasma arc melting treatment of pulverized cement debris spiked by Pb, Cd and Cs, as indicators of typical hazardous metals and radionuclides existed in the low-level mixed waste in the KHNPPs. The final waste form obtained by the test was evaluated for suitability for disposal. The compressive strength was 261.10 MPa, showing much higher values when compared to other waste form products. The compressive strength of both the sample after irradiation with 107 Gy radiation and that after long-term submersion test (90 days) satisfied the disposal criteria. As a result of the leaching test conducted according to the ANS 16.1 test method, it was confirmed that the leaching index satisfies the disposal criteria.

This facility was developed to investigate the characteristics of metal oxide and to secure operational technology through hydrogen supply to 100 kW capacity transferred arc plasma torch and melting furnace under anoxic conditions. Besides, the emission of pollutants generated during operation was minimized by burning the exhaust gases in the next combustion chamber and by applying a SNCR, a scrubber, etc. The main target object was determined as a metal oxides generated as radioactive wastes when dismantling the nuclear power plant. The metal alloy was produced by supplying hydrogen during the melting process of the metal oxide. The reaction equation is as follows: Fe + M(Metal)On + H2(Gas) → FeM + Slag + H2O In this paper, operating conditions according to the melting temperature and hydrogen supply with iron and metal oxides were investigated, and the chemical characteristics of the alloyed metal and Slag were analyzed. The result of this study can be used as fundamental data for the treatment and disposal of metal wastes.

한국원자력연구소 내의 연구용 원자로(TRIGA II, III) 해체 시 발생한 방사성 알루미늄 해체 폐기물의 감용 및 제염 특성을 평가하기 위해 아크로에서 알루미늄의 용융 특성 및 방사성 핵종의 분배 특성에 대한 연구를 수행하였다. 알루미늄 폐기물은 흑연전극(graphite electrode)을 이용한 전기아크로에서 4가지 종류의 플럭스를 함께 첨가하여 용융시켰다. 또한 알루미늄의 용융 시 방사성 핵종의 분배 특성을 고찰하기 위해 알루미늄 시편에 방사성 모의 핵종인 코발트, 세슘, 스트론튬의 화합물을 오염시킨 후 혹연도가니에 넣어 알루미늄 용융실험을 수행하였다. 전기아크로에서 알루미늄의 용융실험을 수행한 결과 플럭스의 종류에 따라 다소 차이는 있으나 플럭스의 첨가에 의해 알루미늄 용융체의 유동성이 증가됨을 확인할 수 있었다. 아크 용융에 의해 생성된 슬래그의 발생량은 플럭스 A와 B를 첨가한 알루미늄 용융실험에 비해 플럭스 C와 D를 첨가한 실험에서 상대적으로 많은 양이 생성됨을 알 수 있었으며, 첨가된 플럭스의 양이 증가할수록 이에 비례하여 슬래그의 발생량이 증가함을 알 수 있었다. 슬래그(slag)의 XRD 분석을 통해 방사성 핵종이 주괴에서 슬래그 상으로 이동한 후 슬래그를 구성하고 있는 산화알루미늄과 결합하여 안정한 화합물로 슬래그 상에 포집됨을 알 수 있었다. 알루미늄 폐기물의 용융시 Co의 분배율은 플럭스를 첨가한 경우에 보다 높은 제염계수를 나타냈으며, 모든 플럭스에서 40% 이상의 제염 효과를 나타내었다. 반면에 휘발성 핵종인 Cs과 Sr은 주괴로부터 98% 이상이 제거되어 대부분이 슬래그상과 분진으로 이동되는 특성을 확인할 수 있었다.