To improve light absorption ability in the visible light region and the efficiency of the charge transfer reaction, Pd nanoparticles decorated with reduced TiO2 nanotube photocatalyst were synthesized. The reduced TiO2 nanotube photocatalyst was fabricated by anodic oxidation of Ti plate, followed by an electrochemical reduction process using applied cathodic potential. For TiO2 photocatalyst electrochemically reduced using an applied voltage of -1.3 V for 10 min, 38% of Ti4+ ions on TiO2 surface were converted to Ti3+ ion. The formation of Ti3+ species leads to the decrease in the band gap energy, resulting in an increase in the light absorption ability in the visible range. To obtain better photocatalytic efficiency, Pd nanoparticles were decorated through photoreduction process on the surface of reduced TiO2 nanotube photocatalyst (r10-TNT). The Pd nanoparticles decorated with reduced TiO2 nanotube photocatalyst exhibited enhanced photocurrent response, and high efficiency and rate constant for aniline blue degradation; these were ascribed to the synergistic effect of the new electronic state of the TiO2 band gap energy induced by formation of Ti3+ species on TiO2, and by improvement of the charge transfer reaction.

To improve photocatalytic performance, a PbS/ZnO/TiO2 nanotube catalyst was synthesized, and its surface characteristics and photocatalytic efficiency were investigated. The hybrid photocatalysts were produced by anodic oxidation and successive ionic layer adsorption and reaction(SILAR). The photocatalytic efficiency was evaluated using the dye degradation rate. The PbS/ZnO/TiO2 photocatalyst significantly enhanced the photocatalytic activity for dye degradation, which was ascribed to the synergistic effect of their better absorption of solar light and a decrease in the rate of excited electron-hole recombination.

The porous Mg3Sb2 based compounds with 60~70% of relative density were prepared by powder compaction at room temperature and reactive liquid phase sintering at 1023 K for 4hrs. The stoichiometric Mg3Sb2 compounds were synthesized from elemental Sb and Mg powder in the mixing range of 61~63 at% Mg. The increased scattering effect due to the micro-pores reduced the mobility of the charge carrier and the phonon, which caused the electrical conductivity and the thermal conductivity to decrease, respectively. But the scattering effect was greater for the electrical conductivity than for the thermal conductivity. Excess Mg alloyed in the Mg3Sb2 compounds decreased the electrical conductivity, but had no effect on the thermal conductivity. On the other hand, the large increase of the Seebeck coefficient was the result of a decrease in the charge carrier density due to the excess Mg. Dimensionless figure of merit of the porous Mg3Sb2 compound reached a maximum value of 0.28 at 61 at% Mg. The obtained value was similar to that of Mg3Sb2 compounds having little pores.

Mg3-xZnxSb2 powders with x = 0-1.2 were fabricated by mechanical alloying in a planetary ball mill with a speed of 350 rpm for 24 hrs and then hot pressed under a pressure of 70 MPa at 773 K for 2 hrs. It was found that there were systematic shifts in the X-ray diffraction peaks of Mg3Sb2 (x = 0) toward a higher angle with increasing Zn for both the powder and the bulk sample and finally the phase of Mg1.86Zn1.14Sb2 was formed at the Zn content of x = 1.2. The Mg3-xZnxSb2 compounds had nano-sized grains of 21-30 nm for the powder and 28-66 nm for the hot pressed specimens. The electrical conductivity of hot pressed Mg3-xZnxSb2 increased with increasing Zn content and temperature from 33 Sm-1 for x = 0 to 13,026 Sm-1 for x = 1.2 at 323 K. The samples for all the compositions from x = 0 to x = 1.2 had positive Seebeck coefficients, which decreased with increasing Zn content and temperature, which resulted from the increased charge carrier concentration. Most of the samples had relatively low thermal conductivities comparable to the high performance thermoelectric materials. The dimensionless figure of merit of Mg3-xZnxSb2 was directly proportional to the Zn content except for the compound with Zn = 1.2 at high temperature. The Mg3-xZnxSb2 compound with Zn = 0.8 had the largest value of ZT, 0.33 at 723 K.

결정성장 도중 전류에 의해 고/액 계면에서 발생하는 Peltier 열을 이용하면 온도구배의 증가와 이에 따른 성장속도의 증가 및 결정성의 향상에 기여할 것이라 예상되어, 고/액 계면에서 복합적으로 발생하는 Peltier 효과를 조사하였다. 전류 밀도, 극성 및 온도구배의 변화에 따른 고상과 액상 및 그 계면에서의 온도변화로부터 이론적 추론에 의해 Peltier 열, Thomson 열 및 Joule 열만의 영향으로 분류할 수 있었고, 고상/액상 계에 대한 Peltier 계수 및 Thomson 계수도 구할 수 있었다.

본 연구의 목적은 장애물 높이에 따른 상지 팔운동 제한이 스텝안정화(stabilization step)에 영향을 주는지 알아보기 위하여 실시하였다. 연구대상자는 대학생 남자 14명, 여자 16명으로 총 30명이였으며, 평균 연령은 21.5세이었다. 스텝 안정화는 FASTEX(functional activity System for testing and exercise, Cybex Division of Lumex, Inc., USA)를 이용하여 측정하였다.