In order to evaluate CMV resistance of the radish inbred lines, leaves of twenties radish (Raphanus sativus L.) inbred lines were mechanically inoculated with a strain of Cucumber mosaic virus (CMV) systematically infecting radish plants, respectively. The inoculated radish plants were incubated at 22°C±3°C and resistance assessment was examined using symptom development for 4 weeks. Based on the reactions of differential radish inbred lines, 11 radish lines were produced mosaic, mottling, yellowing and severe mosaic symptoms by CMV infection. These results were confirmed by RT-PCR analysis of CMV coat protein gene, suggesting that CMV is responsible for the disease symptoms. In contrast, 9 resistant radish lines did not induce systemic mosaic symptoms on upper leaves and chlorosis in stem tissues for 4 weeks, showing that the radish plants did not express any symptoms by 8 weeks. Further examination of CMV infection in the 9 resistance-candidate radish lines showed no CMV infection in systemic leaves of the 9 radish lines. Taken together, these results suggest that the 9 radish lines are highly resistant to CMV.

‘급속면역금나노입자막대 (RIGS) 키트’라 명명된 RIGS 키트는 간단한 면역 흡착막대 방식으로 사용자가 빠르고 편리하게 이용할 수 있으며 토마토덤불위축바이러스 (TBSV)에 대한 현장진단을 하기 위하여 개발되었다. 토끼의 TBSV 항 혈청에서 정제된 면역글로블린G (IgG)는 단백질A 크로마토그래피법으로 정제되었으며 이후 금 나노입자와 결합하여 니트로셀룰로스막에서 진단 선을 표시하도록 고안되었다. TBSV 항체와 비특이적으로 결합하는 단백질A를 같은 진단막대에서 대조선으로 이용되었다. RIGS-TBSV 키트를 이용한 진단은 의심 식물 시료를 완충액이 들어간 플라스틱 봉지에 넣고 착즙후 진단막대기를 넣으면 5-10분 후 결과를 알 수 있도록 고안되었다. TBSV가 감염된 토마토 즙액에 RIGS 막대기를 넣고 진단한 결과 TBSV 농도에 비례하여 진단 선이 형성됨이 관찰되었으며, 이들 키트들은 TBSV와 연관되지 않은 다른 고추 바이러스들에서는 비특이적 반응이 형성되지 않았다. 이런 결과들은 RIGS-TBSV 키트가 TBSV 진단에 다른 어려운 실험이나 기술이 필요하지 않고 쉽게 병원균을 진단 할 수 있다는 것을 의미한다. 그러므로, RIGS-44 TBSV 키트는 TBSV 감염이 의심되는 식물체들의 현장 진단 뿐만 아니라 실험실에서 의 TBSV 진단에 효과적이라 할 수 있다.

‘급속면역금나노입자막대 (RIGS) 키트’라 명명된 빠르며 사용자 편의 및 간단한 면역흡착막대 방식의 키트가 오이모자이크바이러스 (CMV)의 현장진단을 하기 위하여 개발되었다. 토끼의 CMV항혈청에서 정제된 면역글로블린G (IgG)는 단백질A 크로마토그래피법으로 정제되었으며 이후 금나노입자와 결합하여 니트로셀룰로스막에서 진단선 표시하도록 고안되었다.CMV항체와 비특이적으로 결합하는 단백질A를 같은 진단막대에서 대조선으로 이용되었다. RIGS-CMV 키트를 이용한 진단은 의심 식물 시료를 완충액이 들어간 플라스틱 봉지에 넣은 후 착즙 후 진단막대기를 넣으면 된다. 결과는 5-10분 후알 수 있다. CMV가 감염된 고추, 오이 및 멜론의 즙액에RIGS 막대기를 넣고 진단한 결과 CMV 농도에 비례하여 진단선이 형성됨이 관찰되었으며, 이들 키트들은 CMV와 연관되지 않은 다른 고추바이러스들에서 비특이적 반응이 형성되지 않았다. 이런 결과들은 RIGS-CMV 키트가 매우 민감하며,진단에 별 다른 실험실 기술이나 경험이 필요하지 않는 다는것을 의미한다. 그러므로, RIGS-CMV 키트는 CMV 감염이의심되는 식물체들의 현장 진단 뿐만 아니라 실험실에서의CMV 진단에 효과적이다.

바이러스 입자를 감지하는 역전사 핵산 연쇄 증폭법 (VC/RT-PCR)은 감염된 식물종들로부터 핵산 추출 없이 식물바이러스들을 검출 할 수 있다. 본 연구는 VC/RT-PCR 분석법을이용하여 고추를 감염시키는 바이러스들을 효과적으로 진단하기 위하여 새로운 즙액 추출 완충액들이 제작하였다.토마토반점위조바이러스 (Tomato spotted wilt virus;TSWV), 고추약한모틀바이러스 (Pepper mild mottle virus;PMMoV) 및 고추모틀바이러스 (Pepper mottle virus;PepMoV) 진단을 위한 가장 최적화된 추출 완충액은 0.5%sodium sulfate를 포함하는 1.0M Tris (pH 8.0) buffer 였다.고추 바이러스들은 담배 즙액 추출 후 7일까지 검출이 되었으며, 마쇄 직후와 검출 감도는 유의한 차이가 없었다. 반면에,3가지 고추 바이러스들은 고추 즙액 추출 후 2일까지만 바이러스들이 검출되었으며, 검출 감도는 크게 감소하였다.국내 고추 재배 농가들에서 수집한 고추 시료들에서 TSWV,PMMoV, PepMoV의 단독 감염 및 PMMoV와 PepMoV의중복 감염을 선발된 최적 즙액 완충액과 VC/RT-PCR의 조합을 이용하여 동시 진단이 가능하였다.

This study has been carried out to investigate the non-isothermal behaviors and kinetic parameter of calcium carbonate by different thermal analysis methods. At the heating rate of /min, the onset calcination temperature, the peak and final temperatures of calcium carbonate were , , and respectively. As the heating rate of the calcium carbonate increased from /min to /min, the peak temperature increased from to . The activation energies of the calcium carbonate calculated by the methods of Kissinger and Freeman-Carroll were 40.15 kcal/mol and 43.47 kcal/mol, respectively.

스폰지 티타늄으로부터 수산호-탈수소화법(HDH)법으로 제조된 부말에 고상탈산법(DOSS)을 적용시켜 만든 산소 농도 범위 1980~8450 ppm, 입경 25μm 내외의 불규칙 티타늄 분말의 성형 및 소결성을 조사하였다. 250MPa의 가압력으로 냉간압축성형한 결과, 성형밀도는 69.0%~62.3% 범위 내에 있었고 산호함량 증가에 따라 직선 또는 완만하게 감소하였다. 이러한 경향은 티타늄 분말의 경도변화로 설명할 수 있었다. 최고 7%까지의 차이를 보였던 성형밀도에도 불구하고 1100˚C에서 2시간동안 소결한 결과, 산소함량에 무관하게 소결밀도는 90.5±0.5%를 보였으며, 결정립의 크기는60μm 내외의 균일하였고, 가공크기 및 분포도 유사하였다. 소결체의 경도에 미치는 산소의 영향은 실험범위 내에서 VHN(sintered)=135.5+64.3×(wt%O2)의 실험식을 얻었다. 소결체의 파단면 관찰한 결과, 연성에서 취성파괴로의 천이는 소결체에의 산소함량이 2987~5582ppm 사이에서 일어나는 것으로 나타났다.

티타늄 수소화물(TiH2) 분말을 원료로 사용하여 Ti 소결체를 제조하였다. 원료분말은 수소화-탈수소화법(HDH법)에 의해 제조한 상용분말이었으며 비교를 위해 동일한 입도를 갖는 Ti 분말도 함께 소결하였다. TiH2는 소결체의 밀도를 현저하게 촉진하였으며 TiH2→Ti+H2의 탈수소반응에 의해 생성되 청정한 Ti분말이 소결을 촉진하기 때문인 것으로 판단된다. 같은 이유로 TiH2소결체의 산소농도는 Ti 소결체보다 낮게 나타났다. 소결체의 잔류수소는 소결온도가 증가함에 따라 감소하였으며 1200˚C 이상에서는 5 ppm 이하의 낮은 값을 나타냈다. 소결체의 경도는 소결밀도 및 산소량에 비례하는 것으로 나타났다. TiH2분말의 cubic→tetragonal 변태온도는 X-선 회절분석 결과 16~20˚C 구간으로 밝혀졌다.

전자빔 용해법에 의해 고순도 티타늄잉고트 및 버튼시편을 제조하였다. 이들 중 18개의 금속불순물을 GDMS(Glow Discharge Mass Spectrometry)로 그리고 탄소, 질소, 산소의 함량을 고온연소법으로 측정한 후 이들과 전기비저항, 경도와의 관계를 조사하였다. 99%와 99.6%스폰지를 용해한 경우 대부분의금속불순물들이 대폭 감소하는 큰 휘발 정련효과가 나타났으며 비금속불순물들의 경우는 장비의 진공상태에 따라 큰 영향을 받으며 정련효과를 기대할 수 없었다. 금속 불순물중 철은 가장 제거하기 어려운 원소로 밝혀졌으며 이는 원료 스폰기중에서 철이 주불순물이기 때문이며 추가적인 예비정련이 필요한 것으로 나타났다. 상온 및 액체질소온도에서의 전기비저항은 가스불순물의 량이 증가함에 따라 직선적으로 증가하였으며 이들의 저항비(ρRT /ρN2)는 가스불순물의 총량이 1,000ppm이하의 경우 불순물량이 감소함에 따라 급격하게 저하하였으며 이 이상인 경우 완만하게 감소하였다. 이들의 경도는 가스불순물의 량이 증가하였으며 산소당량의 평방근에 비례하는 것으로 나타났다.다.

아크용해로와 진공유도로를 사용하여 니켈-수소 전지의 음극용으로 주목받고 있는 AB2 타입의 ZrV xMn1-xNi1.0, ZrVxMn0.8-xNi1.2, ZrVxMn0.6-xNi1.4합금을 용해하였다. 이들 합금은 용해한 상태에서 C14과 C15의 혼합상을 갖는 것으로 나타났으며 합금조성 및 열처리에 따라 혼합상분율이 크게 변화하였다. 이들의 결정상 및 상분율은 합금원소들의 평균원자반경비(rA/r/sub B)에 따라 결정되는 것으로 밝혀졌으며 특히 열처리한 합금의 경우에는 평균원자반경비가 1.254일때를 경계로 하여 두 상의 명확간 안정구역이 설정되었다. 가압한 분위기에서 아크용해한 경우 합금성분의 손실은 미미하였으나 진공유도로를 사용하여 용해한 경우 Mn이 다량 휘발감소하여 조성이 크게 변화하였다.

플라즈마 회전전극법으로 제조된 Ti-51at%Al 금속간화합물 분말에 함유된 불순물의 함량변화를 분석하였다. 산소와 탄소의 함량은 각각 600 및 200ppm 정도로 분말입도에 따라 변하였으며, 이는 주로 원재료에 포함된 불순물의 영향이었다. AES 분석에 의하면 분말표면 산화물은 주로 Ti 및 Al과 산소 및 탄소의 복합화합물로 구성되었으며, 그 두께는 약 100 및 200μm 크기의 분말에 대하여 각각 7 및 3.4nm 정도로 측정되었다. 분말의 제조로 산소와 탄소의 함량이 오히려 감소되는것의 구체적인 기구는 아직 확인되지 않았으나 플라즈마 고열에 의한 정련현상에 기인하는 것으로 생각된다.

Plasma 용사된 단열피복에 내재하는 기공의 크기, 형상 및 분포는 피복층 자체의 물성에 지대한 영향을 미치므로 이를 용사변수에 따라 조사하였다. MgO 안정화 지르코니아 피복시 도입되는 기공은 미세기공 외에 각각 생성기구가 다른 조대한 기공 즉 구형과 불규칙한 기공, 그리고 crack으로 구성되었다. 용사거리에 따라 기공의 생성과정과 특성이 변하였으며 Plasma 전류 및 가스 유량의 증가에 의해서 기공도는 감소하는 경향을 보였다. Plasma 가스가 N2인 경우가 Ar보다 더 높은기공도를 보였고 전체적으로 단열피복의 기공도는 10~18%였다. Scratch test로 측정된 단열피복층의 상대적인 경도는 기공도와 높은 상관관계를 보였다.