A novel fullerene derivative with photoresponsive azobenzene group was designed and synthesized, and its photoresponsive properties were reported. Starting from 4-nitrophenol, compound 1, which is containing fullerene moiety connected to azobenzene group through covalent linkage was synthesized by 5 steps. All the intermediates and the final compound were characterized by ¹H, 13C-NMR, FAB-Mass or elemental analysis. Compound 1 exhibited the expected photoresponsive behavior. Chloroform solution(10-5M) of it served to maximize the absorption at 351 nm corresponding to the trans-azobenzene chromophore. Irradiation of this solution with 365 nm light resulted in photoisomerization to cis-azobenzene, as evidenced by decrease in the absorbance at 351 nm and an increase in absorbance at 450nm. A hotostationary state was reached within about 150 s. Thermal reversion to the original spectrum was observed over the course of about 6 h at room temperature in the dark. However, exposure to bright sun light for about 5 s also effect almost complete reversion to the trans-isomer. This indicates that there is no strong steric influence on the trans-cis reversible isomerization of compound 1.

We investigated the electrochemical properties for Langmuir-Blodgett (LB) films mixed with 4-octyl-4'-(5-carboxylpentamethyleneoxy)azobenzene (denoted as 8A5H) and phospholipid(L-α-dimyristoylphosphatidylcholine, denoted as DMPC). LB films of 8A5H monolayer and 8A5H-DMPC were deposited by using the Langmuir-Blodgett method on the indium tin oxide(ITO) glass. The electrochemical properties measured by using cyclic voltammetry with a threeelectrode system, an Ag/AgCl reference electrode, a platinum wire counter electrode and LB film-coated ITO working electrode at various concentrations(0.1, 0.5, and 1.0mol/L) of NaClO4 solution. A measuring range was reduced from initial potential to -1350mV, continuously oxidized to 1650mV and measured to the initial point. The scan rates were 50, 100, 150 and 200mV/s, respectively. As a result, LB films of 8A5H monolayer appeared irreversible process caused by only the oxidation current from the cyclic voltammogram and LB films of 8A5H-DMPC mixture were found to be caused by a reversible oxidation-reduction process.

We carried out this experiment to observe electrochemical properties for LB films of phospholipid(Dilauroyl-L-α-Phosphayidylcholine) and 4-octyl-4'-(5-carboxypentamethylene-oxy)azobenzene mixture by the cyclic voltammetry. LB films of 8A5H and 8A5H-DLPC(1:1, 2:1) were deposited by using the Langmuir-Blodgett method on the ITO glass. We determined electrochemical measurement by using cyclic voltammetry with a three-electrode system, An Ag/AgCl reference elect rode, a platinum wire counter electrode and LB film-coated ITO working electrode measured in 0.1, 0.5, and 1.0 mol/L NaClO4 solution. A measuring range was reduced from initial potential to -1350 mV, continuously oxidized to 1650 mV and measured to the initial point. The scan rate were 50, 100, 150 and 200 mV/s. As a result, LB films of 8A5H 8A5H-DLPC appeared irreversible process caused by only the oxidation current from the cyclic voltammogram.

We carried out this subject to observe photoisomerization using 8A5H and phospholipid(DLPC) containing azobenzene group which has reversible to cis-trans by light irradiation. We investigated the photoisomerization and property of the monolayer film on quartz substrate prepared by the mixture of 8A5H and phospholipid deposited using Langmuir-Blodgett(LB) method. It was found that the absorption spectrum of the 8A5H and phospholipid LB monolayer was induced to photoisomerization by alternate light irradiation. And the absorbance of both the solution of mixtures of 8A5H-phospholipid and LB film was reversibly changed by the acid-base exposure and alternate temperatures.

The absorption spectra of synthesis of long chain fatty acid containing azobenzene start from p-(p'-hydroxy phenyl azo)-benzoic acid was investigated by ultraviolet spectrophotometery in chloroform solvent at the various temperature. In addition, The pressure-area of the water-air interface was obtained and the LB film was fabricated onto a quartz slide and quartz crystal by conventional Langmuir-Blodgett(LB) method. The UV absorption spectra of Langmuir-Blodgett(LB) film on quartz slide and spectrum of monolayer formed on quartz crystal have been measured. Long chain fatty acid containing azobenzene are induced phtoisomerization by the application of u. v. and visible light irradiation alternatively the reversibility of phtoisomerization was more clear difference when the number of Cn increased but, not so good at C14-azo. At the pressure-area isotherms, the value of surface pressure increment were decreased when the number of Cn increased. A surface pressure of 20mN/m was obtained as a proper one for a film deposition. The photoisomerization at LB films were induced by application of UV and visible light irradiation alternatively. So the LB film of long chain fatty acid containing azobenzene has possibility to being applied to functional molecular devices such as photomemory and light switching.

The Synthesis of long chain fatty acid containing azobenzene and (Cn-Azo) was optimized, starting from p-(p'-hydroxy phenyl azo)-benzoic acid and the product of reaction containing azobenzene chromophores was investigated by ultraviolet spectrophotometery in chloroform solvent at the various temperature. In addition, Reversibility and stability of azo compounds have been measured by means of Ultraviolet and the structure of these compound were ascertained by means of FT-IR and NMR. Recrystallization of reaction product in the solvent results the experimental yield obtained about 62.93% p-(p'-octadecyloxy phenyl azo)-benzoic acid. Long chain azobenzene derivatives in chloroform solution are induced photoisomerization by u. v. and visible light irradiation. The solution of long chain fatty acids(Cn-Azo) containing azobenzene are possible of being applied to functional molecular devices such as photomemory and light switching.

The Synthesis of azobenzene containing long chain fatty acid and poly vinyl alcohol by esterification reaction(Cn-Azo-PVA) was optimized, starting from P-(P'-hydroxy phenyl azo)-benzoic acid and the product of reaction containing azobenzene chromophores was investigated by ultraviolet spectrophotometery in toluene solvent at room temperature. In addition, UV absorption spectra of Langmmuir Blodggett (LB) film deposited on quartz plate have been measured and the structure of these compounds were ascertained by means of Ultraviolet and FT-IR. Recrystallization of reaction product in the solvent results the experimental yield obtained about 22.27% P-(P'-octadecyloxy phenyl azo)-benzoic acid-poly vinyl alcohol. Long chain azobenzene derivative-poly vinyl alcohols are induced phtoisomerization by u, v, and visible light irradiation. The LB film of azobenzene containing long chain fatty acids(C18-Azo-PVA) are possible of being applied to functional molecular devices such as photomemory and light switching.