We investigated the electrochemical properties for Langmuir-Blodgett (LB) films mixed with fatty acid (8A5H) and phospholipid (DLPE, DMPC, and DPPA). LB films of 8A5H monolayer and 8A5H-phospholipid mixture were deposited using the Langmuir-Blodgett method on the indium tin oxide(ITO) glass. The electrochemical properties measured using cyclic voltammetry with three-electrode system, an Ag/AgCl reference electrode, a platinum wire counter electrode and LB film-coated ITO working electrode at various concentrations(0.1, 0.5, and 1.0 mol/L) of NaClO4 solution. A measuring range was reduced from initial potential to -1350 mV, continuously oxidized to 1650 mV and measured to the initial point. The scan rate was 50, 100, 150 and 200 mV/s, respectively. As a result, LB films of fatty acid and phospholipid (8A5H/DLPE and DPPA) appeared irreversible process were caused by only the reduction current from the cyclic voltammogram and LB film of 8A5H-DMPC mixture was found to be caused by a reversible oxidation-reduction process.

We investigated the electrochemical properties for Langmuir-Blodgett (LB) films mixed with 4-octyl-4'-(5-carboxylpentamethyleneoxy)azobenzene (denoted as 8A5H) and phospholipid(L-α-dimyristoylphosphatidylcholine, denoted as DMPC). LB films of 8A5H monolayer and 8A5H-DMPC were deposited by using the Langmuir-Blodgett method on the indium tin oxide(ITO) glass. The electrochemical properties measured by using cyclic voltammetry with a threeelectrode system, an Ag/AgCl reference electrode, a platinum wire counter electrode and LB film-coated ITO working electrode at various concentrations(0.1, 0.5, and 1.0mol/L) of NaClO4 solution. A measuring range was reduced from initial potential to -1350mV, continuously oxidized to 1650mV and measured to the initial point. The scan rates were 50, 100, 150 and 200mV/s, respectively. As a result, LB films of 8A5H monolayer appeared irreversible process caused by only the oxidation current from the cyclic voltammogram and LB films of 8A5H-DMPC mixture were found to be caused by a reversible oxidation-reduction process.

We studied electrochemical characteristics of Langmuir-Blodgett(LB) films by using cyclic voltammetry with a three-electrode system. An Ag/AgCl as a reference electrode, a platinum wire as a counter electrode and LB film-coated indium tin oxide(ITO) as a working electrode were used to study electrochemical characteristics at a various concentration of NaClO4 solution. LB films were reduced from initial potential to -1350 mV, continuously oxidized to l650mV and returned to the initial point. The scan rate was l00mV/s. The monolayer surface morphology of the LB film have been measured by Atomic Force Microscope(AFM). As a result, We comfirmed that the microscopic properties of LB film by AFM showed the good orientation of momolayer molecules and the thickness of monolayer was 3.5-4.lnm. The cyclic voltammograms(CV) of the ITO-coated glass showed the peak potentials for the reduction-oxidation reation. LB films of 4-octyl-4'-(5-carboxypentamethyleneoxy) azobenzene(8A5H) / L-α-phosphayidyl choline, dilauroyl(DLPC) seemed to be irreversible process caused by only the oxidation current from the cyclic voltammogram. The current of oxidatation increased at cyclic voltammogram by increasing 8A5H density in LB films. The diffusivity(D) of LB films increased with increasing of a 8A5H amount and was inversely proportional to the concentration of NaClO4 solution.

We carried out this subject to observe photoisomerization using 1,2-dioleoyl-sn- glycero-3-phosphocholine(DOPC) mixed with fatty acid containing azobenzene group which has reversible to cis-trans by light irradiation. Spreading solutions for the LB films were prepared in chloroform(5.0×10-5mol/L).We investigated the photoisomerization and property of the organic ultra thin film of fatty acid containing azobenzene was prepared on the hydrophilic ITO(idium tin oxide) glass plate by LB method. As a result, the absorption spectra of 8A5H and DOPC of mixture LB films was induced to photoisomerization by alternating irradiation of ultraviolet and visible light, because the condensation of pure azobenzene monolayers was loosened by the introduction of phospholipid into the monolayers, and the molecular high aggregation in pure azobenzene monolayers is also weakened by the introduction of phospholipid. We found that it was reversibly induced to cis-trans photoisomerization in several solvents and mixture LB films.

We have investgated UV-Vis absorbance to observe the photoisomerization using the mixture solutions in chloroform and LB monolayers mixed with DLPE and 8A5H containing azobenzene which showed reversible cis-trans photoisomerization irradiated by alternate lights. We have found that the absorbance spectrums of the mixture solutions and LB monolayers were reversibly induced to cis-trans photoisomerization irradiated by alternate lights. In addition, the absorbance of both solution and LB monolayer mixed with 8A5H and DLPE were reversibly by alternate temperatures. As a results, the 1:1(by volume) mixture ratio of 8A5H and DLPE was more flexible and reversible cis-trans photoisomerization than the others.