본 논문에서는 압입시험을 통해서 초탄성 재료 물성치를 평가하는 간단한 방법을 제시하였다. 초탄성 재료 모델 중, 3개의 물성치(C10, C20, C30)를 가지는 Yeoh 모델을 선택하여 주연신률로 표현되는 변형률 에너지 밀도를 적용하였다. Yeoh 물성치를 변화시키며, 구형 압입시험 유한요소해석을 수행하여 압입자 반력-변위 곡선을 획득하였다. 압입자 반력-변위 곡선을 3차 다항식으로 근사하였고, 이 다항식을 물성치(C10, C20, C30)의 3차 곱으로 근사된 3차 다항식으로 표현하였다. 압입자 반력-변위 곡선 근사를 위해 회귀분석을 진행하여 수식들의 계수를 결정하였으며, 이 회귀식을 이용하여 초탄성 재료의 물성치를 평가 하였다. 초탄성 재료 물성치 평가를 수행하고 오차를 비교하여 유효성을 보여 주었다.

The objective of this study is to find the optimal size of splined shaft in IMS module. Two methods were used in this study. One is for the investigation of effect of indentation process on the tubular shaft yoke, and another is for the investigation of effect of indentation process on splined shaft. The spline outer size of splined shaft was increased from 0.00mm to 0.20mm. The simulation results were analyzed and compared in terms of under-fill, metal flow, effective strain, Von-mises stress and load characteristics. The indentation load was increased with increasing of spline size. However, in case of 0.15mm outer diameter increasing, the separation load was decreased. The case of 0.10mm diameter increasing was the best spline size based on the low indentation load and high separation load.

Nondestructive instrumented indentation test is the method to evaluate the mechanical properties by analyzing load - displacement curve when forming indentation on the surface of the specimen within hundreds of micro-indentation depth. Resistance spot welded samples are known to difficult to measure the local mechanical properties due to the combination of microstructural changes with heat input. Particularly, more difficulties arise to evaluate local mechanical properties of resistance spot welds because of having narrow HAZ, as well as dramatic changed in microstructure and hardness properties across the welds. In this study, evaluation of the local mechanical properties of resistance spot welds was carried out using the characterization of Instrumented Indentation testing. Resistance spot welding were performed for 590MPa DP (Dual Phase) steels and 780MPa TRIP (Transformation Induced Plasticity) steels following ISO 18278-2 condition. Mechanical properties of base metal using tensile test and Instrumented Indentation test showed similar results. Also it is possible to measure local mechanical properties of the center of fusion zone, edge of fusion zone, HAZ and base metal regions by using instrumented indentation test. Therefore, measurement of local mechanical properties using instrumented indentation test is efficient, reliable and relatively simple technique to evaluate the tensile strength, yield strength and hardening exponent.

In most of sintered metal powder compacts, the sintered density distribution is controlled to be as high and uniform as possible to ensure the required mechanical properties. In general, the density distribution in the compacts is not uniform and not easy to measure. In the present study, a method for measuring the density distribution was developed, based on the indentation force equation by which the hardness and the relative density were related. The indentation force equation, expressed as a function of strength constant, workhardening coefficient and relative density, was obtained by finite element analysis of rigid-ball indentation on sintered powder metal compacts. The present method was verified by comparing the predicted density distribution in the sintered Fe-0.5%C-2%Cu compacts with that obtained by experiments, in which the density distribution was directly measured by machining the compacts from the outer surface progressively.