This study calculated the overall heat transfer coefficient (U-value) of greenhouse covering materials with thermal screens using a simulation model and then estimated the validity of the calculated results by comparison with measured values. The U-value decreased gradually as the thickness of the air space between the double glazing increased, and then remained essentially constant at thicknesses exceeding 25 mm. The U-value also increased with the difference in temperature between the inside and outside of the hot box. The vigorous convective heat transfer between two plastic films caused unsteady heat flow and then created a nonlinear temperature distribution in the air space. The distance did not affect the U-value at distances of 50~200 mm between the plastic covering and thermal curtain. The numerical calculation results, with and without sky radiation, were in accord with the experimental results for a 30°C temperature difference between the inside and outside of the hot box. In conclusion, a reliable Uvalue can be calculated for a temperature difference of 30°C or more between the inside and outside of the hot box.

304L 스테인리스강판은 멤브레인타입 LNG선 단열시스템의 1차 방벽으로 이용된다. 304L 스테인리스강은 변태유기소성(TRIP)강으로 복잡한 재료거동을 보이는데, 이는 소성변형이 발생하는 동안 상변태를 경험하기 때문이다. 본 연구에서는 304L 스테인리스 강의 비선형 기계적 거동분석을 위한 온도의존 일축인장시험을 수행하였으며 재료의 파단이나 비선형 거동을 예측하기 위한 점소성모델을 제안하였다. 수치해석의 결과와 시험 결과를 비교 분석하여 유효성을 검증하였으며 LNG 멤브레인에 대한 적용성을 검토하기 멤브레인 구조시편을 제작하여 구조해석 및 유한요소해석을 수행하였다. 재료모델은 개발 서브루틴을 이용하였으며 ABAQUS 사용자지정 재료 서브루틴을 탑재한 유한요소해석 결과와 극저온 구조인장시험을 수행한 결과를 비교하여 구조적용성을 검증하였다.

Recently, inorganic-organic hybrid materials have attracted much attention not only for their excellent thermal conductivity but also for their flame retardant properties. In this study, the properties of organic-inorganic hybrid insulating materials using inorganic fillers and polyurethane foam with different foaming conditions have been investigated. The addition of 1.5 wt% water to polyurethane as foaming agent shows the best foaming properties. The pore size was decreased in the foaming body with increasing of the CaCO3 addition. The apparent density and thermal conductivity were increased by increasing the CaCO3 addition. With an increasing amount of CaCO3 powder, the flame retardant property is improved, but the properties of thermal conductivity and apparent density tend to decrease. When the addition of fine particles of CaCO3, the apparent density and thermal conductivity were increased and, also, with the addition of coarse particles over 45μm in size, the apparent density and thermal conductivity were increased as well. In this study, the adding of CaCO3 with average particle size of 27μm led to the lowest thermal conductivity and apparent density. After evaluation with different inorganic fillers, Mg(OH)2 showed the highest thermal conductivity; on the other hand, CaCO3 showed the lowest thermal conductivity.

Insulation materials used for building save energy and can be classified into inorganic and organic materials. Organic insulation emits toxic gases in a fire annd has lower water resistance. Inorganic insulation is heavy and has poorer thermal performance than that of organic material. This study evaluated the physical properties and fire resistance of lightweight inorganic insulation foaming material made of waste glass powder. The test results showed that the inorganic material performed well with low density and low thermal conductivity for an insulation material. Foam insulation material manufactured from glass powder was sufficient as a fire-resistant product.

In this study, the use of natural raw material and an inorganic binder such as vermiculite, perlite board prepared by using the inorganic was to prepare a switchboard casing. The characteristics of the basic physical properties such as compression strength of a board made of the inorganic material to the pre-study evaluation therefor.

The energy consumption by buildings approximately reaches 25% of total korea energy consumption. The greatest part in the buildings of the energy consumption is building facade. but a few research projects on concrete comprising more than 70% of outsider of buildings has been tried. This research structural insulation concrete what improved insulation performance using insulation performance improve material