In this paper, AgCl/Ag3PO4/diatomite photocatalyst is successfully synthesized by microemulsion method and anion in situ substitution method. X-ray diffraction (XRD), photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), and ultraviolet-visible spectroscopy (UV-Vis) are used to study the structural and physicochemical characteristics of the AgCl/Ag3PO4/diatomite composite. Using rhodamine B (RhB) as a simulated pollutant, the photocatalytic activity and stability of the AgCl/Ag3PO4/diatomite composite under visible light are evaluated. In the AgCl/Ag3PO4/diatomite visible light system, RhB is nearly 100 % degraded within 15 minutes. And, after five cycles of operation, the photocatalytic activity of AgCl/Ag3PO4/diatomite remains at 95 % of the original level, much higher than that of pure Ag3PO4 (40 %). In addition, the mechanism of enhanced catalytic performance is discussed. The high photocatalytic performance of AgCl/Ag3PO4/diatomite composites can be attributed to the synergistic effect of Ag3PO4, diatomite and AgCl nanoparticles. Free radical trapping experiments are used to show that holes and oxygen are the main active species. This material can quickly react with dye molecules adsorbed on the surface of diatomite to degrade RhB dye to CO2 and H2O. Even more remarkably, AgCl/Ag3PO4/diatomite can maintain above 95 % photo-degradation activity after five cycles.

We studied on the preparation and evaluation of O/W type microemulsion containing "wax, liquid paraffine and quaternary ammonium salt". And also it was obtained to stability of microemulsions by mono ethylene glycol(MEG) addition. The microemulsions were generally prepared at 96~97℃ by the phase inversion method. We used polyoxyethylene(20) sorbitan monooleate(POE(20)SMO) and distearyl dimethyl ammonium chloride(D.D.A.C.) as the emulsifiers at microemulsion preparation. From the results, we could get best condition for microemulsion preparation, in case of oil phase, montanic ester wax ; 1.1wt%, paraffine wax ; 1.1wt%, liquid paraffine ; 3.1wt%, propylene glycol ; 0.6wt% and ethylene glycol monobutyl ether ; 0.6wt%, when the ratio(wt%) of D.D.A.C. and POE(20)SMO were 2 : 3. And also we could obtained that the distributed particle size of the final microemulsions were about 8±1.5nm and the mean particle size was 7±0.5nm. We got following results from final microemulsions that the percent of transmittance; 96~98% at 700nm. And the microemulsion blended with MEG of 5~15wt% showed smaller particle size and more stable distribution than non-containing MEG.

The process variables for the manufacture of translucent microemulsion prepared with 2-octyl dodecanol, 12-hydroxy stearic acid cholesteryl , POE(40)HCO and 1,3-butandiol were examined initially (primary emulsion) and following aging for three months. The techniques empolyed in this study were particle size, turbidity, interfacial tension and microfluidizer. Particle size analysis and turbidity measurement to evaluate the emulsion stability were used. It was concluded that the process of the emulsification was an important indicator of the stability of the translucent microemulsion. From the particle size and and turbidity measurement of translucent microemulsion, adding the surfactant to the oil phase before the emulsification was found to be the most important factor for the stability of emulsions. We found that interfacial tension of the adding the surfactant to the oil phase is lower than that of the adding the surfactant to aqueous phase. In spite of hydrophilic surfactant, adding the surfactant to aqueous phase produced inferior emulsion to that to oil phase.