This study was carried out to investigate the proper wattage and installation distance for the efficient use of nano-carbon fiber infrared heating lamp (NCFIHL), a heating device advantageous for heating energy saving, when the production of watermelon plug seedlings in the plug seedling nursery in winter season. Six small beds were divided into plastic film, and 700 W and 900 W nano-carbon fiber infrared heating lamps were installed at 100 cm above the bed. 1 lamp at central (control), 60 cm interval (2 lamps), and 40 cm interval (3 lamps) heating lamps were installed in each bed inside the greenhouse. All treatments, except the control, were set to keep the night air temperature at 20℃ after lighting the NCFIHL. The leaf temperature showed a tendency to increase fast as the install distance was narrow. The leaf length and leaf width tended to increase as the installation distance of the 700 W heating lamp was narrow. The compactness was high in 700 W heating lamp with 40 cm of installation distance. Therefore, in consideration of maintaining the set temperature at night, installing 700 W electric lamps at 40 cm was an efficient power and installation distance for watermelon grafted seedlings considering economic feasibility.

동절기에 공정육묘장에서 난방 에너지 절감과 우량묘 생산을 위해 나노탄소섬유적외선 난방등(NCFIHL, nanocarbon fiber infrared heating lamp)의 적정 전력과 설치 높이를 구명하는 것이 본 연구의 목적이다. 벤로형 유리 온실 내부에 수박 접목묘를 재배하기 위해 700과 900W NCFIHL을 육묘 베드(1.2 × 2.4m)에서 0.7, 1.0, 및 1.3m 높이로 각각 설치하였다. 수박(Citrullus lanatus (Thunb.) Manst.) ‘지존꿀’과 박(Lagenaria leucantha Rusby.) ‘선봉장’은 각각 접수와 대목으로 사용되었다. 접수와 대목은 편엽합접 방식으로 접목되었다. NCFIHL의 광도는 모든 처리에서 1μmol·m-2·s-1 이하였다. NCFIHL의 광분포는 대부분 적외선 영역에서 나타났다. 외기온도가 10oC 이하일 때 700과 900W NCFIHL을 0.7m 높이로 설치한 처리구와 900W NCFIHL을 1.0m 높이로 설치한 처리에서 야간 설정온도(20oC)를 유지하였다. 열화상 촬영에서는 900W NCFIHL을 0.7m 높이로 설치한 처리에서 가장 빨리 식물체의 온도가 올라갔다. Compactness는 700W NCFIHL을 1.3m 높이로 설치한 처리에서 우수하였다. 결과적으로 700W NCFIHL을 1.0m 이상으로 설치하는 것이 바람직하다고 판단된다.

This review presents current progress in the preparation methods of liquid crystalline nanocarbon materials and the liquid crystalline spinning method for producing nano-carbon fibers. In particular, we focus on the fabrication of liquid crystalline carbon nanotubes by spinning from superacids, and the continuous production of macroscopic fiber from liquid crystalline graphene oxide.

GNPs have several excellent mechanical properties including high strength, a good young’s modulus, thermal conductivity, corrosion resistance, electronic shielding, etc. In this study, CF/GNP/Epoxy composites were manufactured using GNP weight ratios of 0.15 wt%, 0.3 wt%, 0.5 wt%, 0.7 wt% and 1 wt%. The composites were manufactured with a mechanical method (3-roll-mill). Tensile, impact and wear tests were performed according to ASTM standards D3039, D256 and D3181, respectively. The results show that the CF/GNP0.3wt%/Epoxy composites have good mechanical properties, e.g., tensile strength and impact and wear resistance. In this study, both carbon fabric and GNPs were used as reinforcements in the composites. The mechanical properties increased and weight loss decreased as the GNP content in the resin films was increased.

This paper deals with the effects of the surfactant and preplate process (sensitization and activation) on electroless copper plating on carbon nano-fiber (CNF). Ultrasonic irradiation was applied both during dispersion of CNF and during electroless plating containing preplate process. The dispersion of CNF and flatness of the plated copper film were discussed based on the changes in surfactant concentration and preplate process time. It was clearly shown that high concentration of surfactant and long time of preplate process could promote the agglomeration of CNF and uneven copper plating on CNF.

장미 생산농가의 대부분은 겨울철 난방비가 생산비의 가장 큰 몫을 차지한다. 요즘과 같은 고유가 시대에 농가의 부담을 줄이기 위하여 난방비 절감율이 높은 난방시스템에 대한 연구를 수행하였다. 복사열을 이용한 적외선 등 난방의 경우 식물체와 같은 물체를 먼저 가열하여 주변의 기온이 올리는 방식으로 빠르게 온도를 높일 수 있고 경유를 이용한 난방방식에 비해 비용이 절감되는 장점이 있다. 농가에 설치된 나노탄소 섬유 적외선 등 난방시스템의 현지조사를 실시하여 난방효과 및 난방비 절감율을 분석하고, 나노탄소섬유 적외선 등 난방시스템과 전기히터 난방시스템에서 생산된 '오렌지 플레쉬' 장미의 생육과 절화수명을 조사하였다. 나노탄소섬유 적외선 등의 경우 온실 내부 공기 설정온도가 20℃인 경우 식물체 온도는 1~2℃정도 더 높게 나타났을 뿐만 아니라 베드와 근권부 온도는 17~19℃ 정도로 유지하는 등 우수한 난방의 효과를 알 수 있었고, 전기히터 난방시스템과 온수보일러 난방시스템의 추정 난방비를 비교한 결과 난방비 절감 효과가 아주 높게 나타났다. 장미의 생육을 조사한 결과 전기히터 난방시스템에서 생육한 장미와 차이가 없었으며 화색이나 염색의 발현이 더 좋았다. 절화수명에서는 나노탄소섬유 적외선 등에서 생육한 장미가 생체중과 수분 흡수량이 높아 다소 더 길어진 절화수명을 뒷받침 해 주었다.