In this study, a method to remove residual powder on a multi-layered graphene and a new approach to transfer multi-layered graphene at once are studied. A graphene one-step transfer (GOST) method is conducted to minimize the residual powder comparison with a layer-by-layer transfer. Furthermore, a residual powder removing process is investigated to remove residual powder at the top of a multi-layered graphene. After residual powder is removed, the sheet resistance of graphene is decreased from 393 to 340 Ohm/sq in a four-layered graphene. In addition, transmittance slightly increases after residual powder is removed from the top of the multi-layered graphene. Optical and atomic-force microscopy images are used to analyze the graphene surface, and the Ra value is reduced from 5.2 to 3.7 nm following residual powder removal. Therefore, GOST and residual powder removal resolve the limited application of graphene electrodes due to residual powder.

The effects of residual impurities on solid state sintering of the powder injection molded (PIMed) W-15wt%Cu nanocomposite powder were investigated. The W-Cu nanocomposite powder was produced by the mech-ano-chemical process consisting of high energy ball-milling and hydrogen reduction of W blue powder-cuO mixture. Solid state sintering of the powder compacts was conducted at for 2~10 h in hydrogen atmosphere. The den-sification of PIM specimen was slightly larger than that of PM(conventional PM specimen), being due to fast coalescence of aggregate in the PIM. The only difference between PIM and PM specimens was the amount of residual impurities. The carbon as a strong reduction agent effectively reduced residual W oxide in the PIM specimen. The formed by reduction of oxide disintegrated W-Cu aggregates during removal process, on the contrary to this, micropore volume rapidly decreased due to coalescence of the disintegrated W-Cu aggregates during evolution of CO.It can be concluded that the higher densification was due to the earlier occurred Cu phase spreading that was induced by effective removal of residual oxides by carbon.

수산화물법에 의해 제작된 α-stannic acid의 열분해 거동과 SnO2분말의 성질에 미치는 잔류염소이온의 영향을 관찰하였다. SnCl4와 NH4OH 수용액을 중화시켜 α-stannic acid침전물을 제작하고 NH4NO3수용액으로 세척하였다. 분말내의 잔류 염소이온의 양을 주절하기 위하여 세척정도를 3단계로 조정하였다. 세척후 100˚C에서 건조하고, 500˚C ~ 1100˚C에서 하소함으로써 SnO2분말을 제조하였다. α-stannic acid의열분해 거동ㅇ르 DT-TGA 와 FTIR을 통하여 관찰하고, SnO2분말의 조성과 입자크기 및 비표면적을 각각 AES, TEM 및 BET을 통하여 측정하였다. 잔류 염소이온 양이 감소되면, 저온 하소시 일차입자의 상대적 크기가 커지는 반면 고온하소시에는 상대적으로 감소되었ㄷ. 잔류 염소이온의 일부는 α-stannic acid내의 격자산소 자리에 위치함으로써, 저온가열시 결정수탈리와 결정화를 지연시키고 또한 고온가열시에는 이의 증발에 의해 산소공공이 생성되어 소결을 촉진시킨다고 제의하였다.