Purpose : Ophthalmic soft contact lens using functional silicone monomer were manufactured and the physical properties of copolymerized materials were analyzed. Methods : The materials for ophthalmic hydrogel contact lenses were polymerized by adding 1,3-bis(TDS) and acrylated poly-(dimethyl siloxane) to DMA, HEMA and cross-linking agent(EGDMA) which are commonly used in ophthalmic hydrogel contact lenses. The hydrogel ophthalmic lens was manufactured by cast mould method. The manufactured ophthalmic hydrogel contact lenses were stored in a 0.9% NaCl normal saline for 24 hrs. And also, for the utility of functional silicone monomer as a high gas permeability and visible light transmittance material for ophthalmologic devices, the oxygen permeability, spectral transmittance and water contact were measured. Results : The value of oxygen permeability ranges from 16.83 to 36.59 x    ×     sec ×  ×   . The results showed that the average value of water content decreased as the ratio of additive increased. The visible light tansmittance of copolymerized ophthalmic soft contact lenses, was in the range 89~ 92%. Conclusions : The material containing acrylate poly-(dimethyl siloxane) and methacrylate siloxane is expected to be used usefully as a material for high oxygen permeability hydrogel contact lens.

목적: 새로 합성한 silicone monomer인 3-[Tris(vinyldimethylsiloxy)silyl]propyl methacrylate(V-TRIS)를 이용하여 제조한 Silicone hydrogel contact lens(SiHy)와 제조 과정 에서 에탄올을 첨가하여 만든 SiHy의 광투과율과 함수율에 대해 살펴보고자 한다. 방법: 3-(Trimethoxysilyl)propyl methacrylate와 chlorodimethylvinylsilane을 반응하여 Silicone을 4개 함유하는 V-TRIS를 합성하였다. Figure. 1. Reaction scheme for the synthesis of V-TRIS. V-TRIS를 전체 무게의 10%, 20% 만큼 첨가하고 2-hydroxyethyl methacrylate(HEMA), Azobis isobutyronitrile(AIBN), Ethylene glycol dimethacrylate(EGDMA), N-vinyl-2 -pyrrolidone(NVP) 등과 열중합하여 SiHy를 제조하였다. 에탄올은 전체무게의 15%를 첨가하 였다. 제조된 SiHy는 증류수에 24시간 동안 담가둔 후 함수율을 측정하였으며, 파장 400~1100nm 범위에서 UV spectrophotometer(JENWAY, Genova Nano)를 이용하여 광투과 율을 측정하였다. 결과: Table 1. Optical Transmittance and water contents of SiHy with ethanol dilution. V-TRIS를 이용한 SiHy의 함수율은 32~35% 정도로 나타났다. SiHy 제조과정에서 에탄올을 첨가한 경우 광투과율과 함수율이 각각 증가하였다. 결론: 친수성인 HEMA와 소수성인 silicone monomer, V-TRIS가 서로 잘 섞이지 않아 상분리 현상이 발생한다. 이로 인해 SiHy의 광투과율이 낮아지게 되는데 친수성 및 소수성 물질에 동시에 잘 섞이는 알콜기를 포함하는 에탄올을 첨가함으로서 HEMA와 V-TRIS가 상분리 현상 없이 잘 섞이게 되어 광학적으로 투명한 SiHy를 얻을 수 있다.