This paper, the hardness of the silicone rubber wire for 50, 60 degrees, 70 degrees High Temperature Vulcanizing (HTV) method using specimens were fabricated. In this paper, in order to investigate the dielectric properties of silicone rubber for wire specimens, the temperature range of 30℃～170℃, the frequency range from 100Hz～4.5MHz report surveyed about the frequency and temperature dependent properties.

An inorganic filling agent, ATH (alumina trihydrate) was used to induce inorganic-organic coupling by mixing with stearic acid, acryl silane, vinyl silane as surface treatment agents in order to apply as a high voltage insulating material. Volumetric resistivity was shown to vary with surface treatment agents, and the highest value was obtained in case of the mixture with vinyl silane. The dielectric breakdown intensity was shown to decrease gradually and saturate to a stable value, possibly due to the increase of cross link density in the vinyl radicals introduced to silica surface, resulting in stable dielectric breakdown intensity in the final stages. Tracking and flame retardant properties were also shown to be the best among the samples investigated in this study.

실리콘 고무(고무상고분자)와 폴리스틸렌(유리상고분자)을 이용하여 true-IPN을 합성하였다. 합성방법은 단계(sequential) IPN(interpenetrating polymer net- work) 제조방법이며, 이때 IPN 내의 폴리스틸렌 함량을 10-70 wt%로 변화시켜 폴리스틸렌의 함량에 따른 산소/질소의 투과특성을 조사하였다. FTIR과 NMR의 결과 단계IPN 합성법으로 실리콘고무-폴리스틸렌의 IPN분리막이 제조되었음을 확인하였으며, 열분석 결과 폴리스틸렌의 함량이 증가할수록 실리콘고무와 폴리스틸렌의 혼합도(degree of mixing)가 증가한다는 것을 알 수 있었다. 기체투과특성 조사에서는 폴리스틸렌의 함량이 증가할수록 산소투과도는 감소하는 경향이 있었으나, 50wt% 폴리스틸렌이 함유된 분리막에서 일시적인 증가를 보여주었다. 또한 선택도는 폴리스틸렌의 함량이 증가하면서 약간 증가하다, 50wt% 폴리스틸렌이 함유된 분리막에서 20.6% 향상된 최대 값을 얻을 수 있었다. 이것은 폴리스틸렌이 50wt%인 분리막에서 IPN의 상호보완적인 성질이 가장 잘 나타난 결과라고 할 수 있다