        1.
        2021.06 KCI 등재 구독 인증기관 무료, 개인회원 유료
        We report the comparative study of electronic and optical properties of (6,1) SWCNT from GGA and DFT-1/2 methods. (6,1) SWCNT is a low-bandgap semiconductor, which falls within ( n1 − n2)/3≠ integer. The calculated bandgaps are 0.371 eV and 0.462 eV from GGA and DFT-1/2, respectively. Thus, DFT-1/2 enhanced the electronic bandgap by 24.52%. From both GGA and DFT-1/2 approaches (6,1) SWCNT exhibits an indirect bandgap along Γ − Δ symmetry. However, the percentage change in direct–indirect bandgap is negligibly small, i.e., 4.1% and 3.7% from GGA and DFT-1/2, respectively. The refractive index measured along x-axis ( n x ) approaches unity, indicating transparent behaviour, while that along z-axis ( n z ) goes as high as ∼3.82 for photon energy 0.0 − 0.15 eV, exhibiting opaque behaviour. Again, the value of n z drops below unity at photon energy ∼0.18 eV and again approaches ∼ 1 for higher energy ranges. The optical absorption is highly anisotropic and active within the infrared region.
        4,000원
        2.
        2013.12 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Flexible transparent conducting films (TCFs) were fabricated by dip-coating single-wall carbon nanotubes (SWCNTs) onto a flexible polyethylene terephthalate (PET) film. The amount of coated SWCNTs was controlled simply by dipping number. Because the performance of SWCNT-based TCFs is influenced by both electrical conductance and optical transmittance, we evaluated the film performance by introducing a film property factor using both the number of interconnected SWCNT bundles at intersection points, and the coverage of SWCNTs on the PET substrate, in field emission scanning electron microscopic images. The microscopic film property factor was in an excellent agreement with the macroscopic one determined from electrical conductance and optical transmittance measurements, especially for a small number of dippings. Therefore, the most crucial factor governing the performance of the SWCNT-based TCFs is a SWCNT-network structure with a large number of intersection points for a minimum amount of deposited SWCNTs.
        3,000원
        3.
        2009.03 KCI 등재 구독 인증기관 무료, 개인회원 유료
        We measured the non-carbon content of single-walled carbon nanotubes (SWCNTs) in SWCNT soot using thermogravimetric analysis. The weight increased percentage by the oxidation of metal in the raw soot is well obtained by TGA graph which was confirmed with ICP-AES, XRD, and XPS. This work will be very useful for the purity precise evaluation of SWCNT with UN-vis-NIR spectroscopy.
        3,000원
        4.
        2008.05 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        A simple method to deposit carbon nanotube films uniformly on large area substrates using an arc discharge method is reported in this paper. The arc discharge method was modified to deposit carbon nanotube films in situ on the substrates. The substrates were scanned several times over the arcing point for a uniform film thickness. Deposition was carried out under variable dc bias conditions at 600 torr of H2 gas. The thickness uniformity of the single-wall carbon nanotube films as characterized by a four-point probe was within 30% deviation. The morphology and crystal quality of the single-wall carbon nanotube film were also characterized by field emission scanning electron microscopy and Raman spectroscopy.
        4,000원