Four types of high Mn TWIP(Twinning Induced Plasticity) steels were fabricated by varying the Mn and Al content, and the tensile properties were measured at various strain rates and temperatures. An examination of the tensile properties at room temperature revealed an increase in strength with increasing strain rate because mobile dislocations interacted rapidly with the dislocations in localized regions, whereas elongation and the number of serrations decreased. The strength decreased with increasing temperature, whereas the elongation increased. A martensitic transformation occurred in the 18Mn, 22Mn and 18Mn1.6Al steels tested at −196 oC due to a decrease in the stacking fault energies with decreasing temperature. An examination of the tensile properties at −196 oC showed that the strength of the non-Al added high Mn TWIP steels was high, whereas the elongation was low because of the martensitic transformation and brittle fracture mode. Although a martensitic transformation did not occur in the 18Mn1.9Al steel, the strength increased with decreasing temperature because many twins formed in the early stages of the tensile test and interacted rapidly with the dislocations.

In the present study, the tensile properties and dynamic strain aging of an Fe-24.5Mn-4Cr-0.45C alloy were investigated in terms of strain rate. During tensile testing at room temperature, all the stress-strain curves exhibited serrated plastic flows related to dynamic strain aging, regardless of the strain rate. Serration appeared right after yield stress at lower strain rates, while it was hardly observed at high strain rates. On the other hand, strain-rate sensitivity, indicating a general relationship between flow stress and strain rate at constant strain and temperature, changed from positive to negative as the strain increased. The negative strain-rate sensitivity can be explained by the Portevin Le Chatelier effect, which is associated with dynamic strain aging and is dependent on the strain rate because it is very likely that the dynamic strain aging phenomenon in high-manganese steels is involved in the interaction between moving dislocations and point-defect complexes.

The purpose of this study was to evaluate the tensile fracture energy absorption capacity of hybrid fiber reinforced cement composite by strain rate. Experiment result, it was confirmed that PVA suppressed the microcrack around the HSF at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the HSF.

CFRP (Carbon Fiber Reinforced Plastic) has high tensile strength, light weight, and excellent corrosion resistance, so it is used for construction such as seismic reinforcement and explosion proof in construction area. Dynamic loads, such as earthquakes and explosions, cause rapid deformation of the material and the material behaves differently from its static condition. Therefore, in this study, tensile tests of CFRP were conducted under static and dynamic loads, and the tensile performance of was evaluated according to the strain rate.

The purpose of this study was to evaluate the direct tensile fracture behavior of steel fiber hybrid reinforced cement composite by strain rate. Experiment result, it was confirmed that SSF suppressed the microcrack around the HSF at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the HSF.

The purpose of this study was to evaluate the direct tensile fracture behavior of fiber hybrid reinforced cement composite by strain rate. Experiment result, it was confirmed that PVA suppressed the microcrack around the steel fiber at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the steel fiber.

In this study, the fiber blending ratio and strain rate effect on the tensile behavior of hybrid fiber reinforced cement composite was evaluated. Hooked steel fiber and polyvinyl alcohol fiber were used for reinforcing fiber. The fiber blending ratio of HSF+PVA were 1.5+0.5, 1.0+1.0 and 0.5+1.5vol.%. As a results, the tensile strength, strain capacity and fracture toughness of the hooked steel fiber reinforced cement composites were improved by the increase of the bond strength of the fiber and the matrix according to increase of strain rate. However, the tensile stress sharply decreased after the peak stress because of the decrease in the number of straightened pull-out fibers by micro cracks in the matrix around hooked steel fiber. On the other hand, PVA fiber showed cut-off fracture at strain rate 10-6/s with multiple cracks. However, at the strain rate 101/s, the multiple cracks and strain capacity were decreased because of the pull-out fracture of PVA fiber. The HSF1.5PVA0.5 shown the highest tensile strength because the PVA fiber suppressed the micro cracks in the matrix around the hooked steel fiber and improved the pull-out resistance of hooked steel fiber. Thus, DIF of strain capacity and fracture toughness of HSF1.5PVA were greatly improved. In addition, the synergistic response of fracture toughness was positive because the tensile stress was slowly decreased after the peak stress by improvement of the pull-out resistance of hooked steel fiber at strain rate 101/s

The purpose of this study was to evaluate the tensile fracture behavior of fiber hybrid reinforced cement composite according to the strain rate. Experiment result, it was confirmed that the number of cracks and the strain capacity tended to decrease with increasing PVA fiber volume fraction at the strain rate of 101/s.

본 연구에서는 유압식 급속재하 시험 장치를 제작하여 변형 속도에 따른 후크형 강섬유 및 폴리아미드 섬유보강 시멘트 복합체의 압축강도 및 인장강도 특성을 평가하였다. 그 결과, 변형 속도가 증가함에 따라 압축강도, 최대 응력 점에서의 변형 및 탄성계수는 증가하였으 며, 섬유 종류 및 혼입률은 변형 속도에 의한 압축강도의 영향은 크지 않았다. 본 연구에서 평가된 압축강도의 DIF는 CEB-FIP model code 2010 에 비해 상회하였으며, ACI-349의 예측값과 유사한 경향이 나타났다. 인장특성의 경우에도 변형 속도가 증가함에 따라 인장강도와 변형능력 이 크게 향상되었다. 후크형 강섬유보강 시멘트 복합체는 변형 속도가 증가함에 따라 섬유와 매트릭스의 부착력이 증가하는 것에 의해 인장강 도와 변형능력이 크게 향상되었으며, 섬유가 매트릭스로부터 인발되는 파괴 특성이 나타났다. 한편, 폴리아미드 섬유보강 시멘트 복합체의 경 우 섬유와 매트릭스의 부착력이 크기 때문에 섬유가 매트릭스로부터 인발되지 않고 끊어지는 파괴 특성이 나타났으며, 폴리아미드 섬유보강 시멘트 복합체의 인장특성에 대한 변형 속도 효과는 섬유의 인장강도에 큰 영향을 받는 것으로 판단되었다. 이러한 결과로부터 폴리아미드 섬 유보강 시멘트 복합체의 인장강도에 대한 변형 속도의 효과는 후크형 강섬유의 부착력에 대한 민감도 보다 큰 것으로 사료된다.