In order to improve resistant properties of water-borne acrylic pressure sensitive adhesives(PSAs) for automobiles, this study was carried out. Removable PSAs for automobiles were synthesized by emulsion polymerization of monomers, n-butyl acrylate(BA), n-butyl methacrylate(BMA), acrylonitrile(AN), acrylic acid(AA) and 2-hydroxyethyl methacrylate(2-HEMA), and AA and 2-HEMA could act as functional monomers for crosslink. Emulsion polymerization was carried out in a semi-batch type reactor. Water resistance, heat resistance, acid resistance, alkali resistance and smoke resistance were examined. As a result, water resistance increased with the amount of BMA, however, the effect of BMA content on the water resistance was insignificant at a range of over 14 wt%. The water resistance also increased with the amount of functional monomers, AA and 2-HEMA. The prepared PSAs satisfied all the standard for automobiles except heat resistance. However, the heat resistance comes nearly up to the standard. Also, acid resistance, alkali resistance and smoke resistance of the prepared PSAs satisfied with the standard.

Removable protective adhesives for automobiles were synthesized by an emulsion polymerization of monomers such as n-butyl acrylate (BA), n-butyl methacrylate (BMA), acrylonitrile (AN), acrylic acid (AA) and 2-hydroxyethyl methacrylate (2-HEMA), in which AA and 2-HEMA were functional monomers. Potassium persulfate (KPS) was used as an initiator and sodium lauryl sulfate (SLS) was used as an emulsifier, and polyvinyl alcohol (PVA) was used as a stabilizer. Emulsion polymerization was carried out in a semi-batch type reactor. Tensile strength, extension, peel strength, viscosity and solid content of the synthesized adhesives were tested. The optimum physical properties of the removable protective adhesives for automobiles were obtained with the composition of 0.43 mole BA, 0.57 mole AN, 0.21 mole BMA, 0.03 mole AA, and 0.03 mole 2-HEMA.