논문 상세보기
pp.117-124
This study developed a flame-retardant fiber-reinforced composite material that satisfies the required regulations of railway vehicle interior parts for the purpose of reducing weight and simplifying the production process using SMC(sheet molding compounds) composite materials. It is essential to secure flame-retardant performance that minimizes flames and smoke for the safe evacuation of passengers in case of fire for interior parts of railway vehicles. In this study, the resin for SMC was developed by adding various flame retardant materials such as vinyl ester (halogen-based and phosphorus-based) and antimony trioxide, and chopped glass fibers were used as the reinforcing material. As a result of preparing specimens for phosphorus-based and halogen-based SMC materials, and comparing the flame retardant performance, the phosphorus-based SMC material had an oxygen index of 36.1, smoke density (1minute 30 seconds, 4minutes, 10minutes) of 1.7, 51.5, 195.1. It was measured with a toxicity index of 0.05 R and average heat for sustained burning of 4.5MJ/m, which satisfies all the flame retardant standards required for interior parts of railway vehicles, and it was found that most of the performance was better than that of halogen-based SMC.