When a rapid groundwater inflow is introduced from the adjacent rock mass in the early stage of disposal, hydraulic pressure build-up occurs, which may cause piping erosion at the buffer material itself and the interface of the gap-filling material. Such piping erosion in compacted bentonite buffer via interaction between the buffer and the adjacent rock mass may deteriorate the performance of the buffer material. Therefore, it is necessary to understand the conditions and scenarios in which the piping phenomenon around the buffer material occurs for the long-term health of the repository. In this study, laboratory-scale experimental tests of piping erosion in buffer and interfacial rock was introduced. ø 100 mm × 200 mm height compacted bentonite specimens were placed in a cylindrical acetal cell, and the distilled water was continuously injected at a flow rate of 0.068 L/min using a dual syringe pump. The inflow of water was generated from the bottom and side cell of buffer material. During water injection, injected water pressure and amount were measured with visual observation. The results showed that the external saturation of buffer firstly occurs followed by piping crack generation along the wetting front. The additional piping channels were generated and merged with others. As the injection stopped, the swelling and self-sealing behavior of buffer material were observed. Moreover, X-ray CT scanning of the cell was conducted after the piping simulation to analyze the piping channels and saturation depth. The results highlight the piping erosion phenomenon mainly occurs due to the presence of a gap outside the buffer material. Further experimental cases is need to comprehensively understand piping phenomena in buffer material for assessing the long-term stability of underground radioactive waste disposal systems.

The backfill refills the deep geological disposal system after the installation of buffer in the disposal hole. SKB and Posiva have established the safety function for the backfill such as hydraulic conductivity of 10-10 m/s and swelling pressure of 0.2 MPa. The study on the thermal properties is required for the evaluation of performance design and long-term stability of backfill, since the thermal condition affects the hydraulic and mechanical behavior of backfill. Thermal conductivity is a key characteristic of thermal properties due to heat dissipation from spent fuel. In this study, thermal conductivities of bentonite-sand mixed blocks were measured. The silica sands were used instead of the crushed rock with bentonil-WRK, one of the candidate bentonite of the Korean repository system. The effects of size distribution and mass ratio of sand were evaluated. Four different size of silica sand (i.e., 0.18-0.25, 0.7-1.12, 1.6-2.5, 2.5-5.0 mm) and five mixing ratio (i.e., 1:9, 2:8, 3:7, 4:6, 5:5 of bentonite and sand) were used for characterization of thermal conductivity. As a result, the thermal conductivities were measured ranging from 1.6 to 3.1 W/m∙K depending on the size and mass ratio of the sand. The smaller the size or higher the mixing ratio of sand or the higher the water contents, the higher the thermal conductivity on the surface of backfill block. The higher compressing pressure induce higher thermal conductivity. Meanwhile, the feasibility study of backfill block productivity was reviewed according to the variables of this study. The excessive sand ratio and water contents lead to poor quality that results in the failure of the block. In Korea, the research of backfill is only now in fundamental steps, thus the results of this study are expected to use for setup the experimental conditions of hydraulic and mechanical performance, and can be used for the design of safety function and evaluation of long-term stability for deep geological disposal system.

The high-level waste disposal system is an underground structure exposed to complex environmental conditions such as high temperature, radiation, and groundwater. The high-level waste disposal causes structural cracks and deterioration over time. However, since the high-level waste disposal system is a structure that should be operated for a very long time, developing a high-durability monitoring sensor to detect cracks and deterioration is essential. The durability of the sensor can be evaluated by predicting the expected life through the accelerated life test, one of the reliability qualification tests. The most important factor in the accelerated life test design is setting the harsh stress level. This study figured out the harsh stress level of the piezoelectric sensor, which is commonly used for underground structure monitoring. It is possible to determine the appropriate stress level for the accelerated life test by investigating the harsh stress level for the temperature factor. It will contribute to more accurate life expectancy prediction.

The structural integrity of concrete silos is important from the perspective of long-term operation of radioactive waste repository. Recently, the application of acoustic emission (AE) is considered as a promising technology for the systematic real-time health monitoring of concrete-like brittle material. In this study, the characteristics of AE wave propagation through concrete silo of Gyeongju radioactive waste repository were evaluated under the effects of groundwater and temperature for the quantitative damage assessment. The attenuation coefficients and absolute energies of AE waves were measured for the temperature cases of 15, 45, 75°C under dry and saturated concrete specimens, which were manufactured based on the concrete mix same as that of Gyeongju concrete silo. The geometric spreading and material loss were taken into account with regard to the wave attenuation coefficient. The attenuation coefficient shows a decreasing pattern with temperature rise for both dry and saturated specimens. The AE waves in saturated condition attenuate faster than those in dry condition. It is found that the effect of water content has a greater impact on the wave attenuation than the temperature. The results from this study will be used as valuable information for estimating the quantitative damage at the location micro-cracks are generated rather than the AE sensor location.