Open clusters are useful tools to investigate the structure and evolution of the Galactic disk. We have started a long-term project to obtain UBVI CCD photometry of open clusters which were little studied before, using the Doyak 1.8 m telescope of Bohyunsan Optical Astronomy Observatory in Korea. The primary goals of this project are (1) to make a catalog of UBVI photometry of open clusters, (2) to make an atlas of open clusters, and (3) to survey and monitor variable stars in open clusters. Here we describe this project and report the first results based on preliminary analysis of the data on four open clusters in the survey sample: Be 14, Cr 74, Biu 9, and NGC 2355. Isochrone fitting of the color-magnitude diagrams of the clusters shows that all of them are intermediate age to old (0.3-1.6 Gyrs) open clusters with moderate metallicity.
Powder forging with a back pressure was investigated for production of automobile and compressor parts made of a rapidly solidified Al-Si alloy powder. Disk-shaped green compacts made of a rapidly solidified Al-Si alloy powder were hot forged, and hubs were formed by loading back pressure on their top. The influences of the back pressure and die temperatures on forgeabiliy and properties of parts made of a rapidly solidified Al-Si alloy powder were examined. This method was also applied to the production of a scroll part. The results of these studies are summarized as follows : 1. A back pressure on the hub top is very effective for consolidation and preventing crack formation in the hub. 2. When a back pressure tess than 98 MPa is applied, the forging pressure increases by the same amount of the applied back pressure. With more than 98 MPa, the forging pressure increases further due to an increased friction at the hub side. 3. Die temperatures higher than approximately 670k are needed in order to consolidate well the hub top without cracks.