The N-docosyl N'-methyl viologen-(TCNQ)2, (DMVT) was synthesized. We investigated the π-A isotherm of DMVT to find the optimal deposition condition. Temperature-dependent current-voltage characteristics of the DMVT LB films shows that there is an increase in conductivity at 330K or so. The in-plane electrical conductivity at room temperature is in the range of 10-7~10-6S/cm. From the plot of logarithmic conductivity as a function of reciprocal temperature, two types of activation energies, 0.04eV and 0.73eV, were obtained depending on the temperature range. The Ohmic behaviour was observed below 0.6V and the Schottky effect was confirmed at 2.5~6V, when the I-V characteristics was measured with Al/LB film/Al structure. I-V measurement for Al/LB film/ITO structure showed the asymmetrical I-V relationship, which resulted from the rectification property.

The polyimide film surface was modified with KOH aqueous solutions or sulfuric acid. The film thickness was increased by about 10% through the modification of film surface. Hydrolysis of amide bonds and hydration of water induced the increase. The polarity of the film surface increased and identified by contact angle measurement. The depth and roughness of modified was increased. After treatment of surface with water, alkyl and 4-pentyloxyaniline were introduced on the film surface by complex formation between anionic species formed on the imide surface and ammonium ion. The newly introduced alkyl group was identified by FT-IR spectroscopy. Surface polarity reduced dramatically and the roughness was increased after introduction of ammonium salt.