Poly(oxypropylene-oxyethylene glycol) block copolymer(PBC) oil dispersant, which has low toxicity, high biodegradability, and an excellent dispersion efficiency to crude oils and weathered W/O emulsion was prepared by blending PBC, poly(oxyethylene) oleate, and sorbitan monooleate. The dispersing efficiency was measured by swirling flask method. The PBC oil dispersant had an excellent dispersing efficiency to weathered oil products formed as stable W/O emulsion, and the low toxicity, such as 4000 ppm to Oryzias Latipes(24 hr, TLM), Brine Shrimp Artemia(24 hr, TLM).

Fireproofing polyolefin nanocomposite for the application of power distributing panel was prepared by compounding linear low density polyethylene(LLDPE), decabromodiphenyl oxide (DBDPO), Sb2O3 as flame retardant agents, and modified nano clay as filler. The optimized formulation ratio of compounds to prepare the fireproofing polyolefin nanocomposite was obtained. The flame retardant properties for nanocomposite prepared by compounding 22.5 phr of nano clay and 18 phr of DBDPO based on 100 phr of LLDPE were shown that the combustion time. 10~18 s, combustion distance, 12~15 mm and non-melt dropping characteristics. In particular. the content of DBDPO in nanocomposite could be decreased to 18 phr from 40 phr DBDPO for fireproofing composite containing 30 phr of clay. The electrical properties measured from tracking test, had an excellent antitracking properties by not showing the phenomenon of leakage current and sparking.

Polyoxyethylene monooleate was prepared by addition of ethylene oxide to oleic acid. And also, polyoxyethylene monooleate type oil dispersant was prepared by blending polyoxyethylene monooleate, n-paraffine, sorbitan monooleate, sorbitan monopalmitate, and palm oil. Dispersion efficiency test was carried out by vertical shaking flask and swirling flask methods. Low toxic oil dispersant was prepared with polyoxyethylene monooleate, which has high biodegradability and excellent dispersion efficiency on crude oils and weathered W/O emulsions with high viscosity, and its dispersion efficiency was measured to various crude oils and weathered oils.

Low toxic concentrated oil dispersant using n-Paraffin and Di(ethylene glycol)mono butylether mixed solvent was prepared, and tested by oil dispersant performance test method, and oil dispersant efficiency was measured using vertical shaking method to 3 kinds of Crude oil, Bunker oil and W/O emulsions with different physical properties by appling the prepared dispersant. Although toxicity test was performed with Flat fish and Rock fish by appling the mixed oils emulsified using prepared oil dispersant, couldn't find the toxicity to them. Concentrated oil dispersant prepared has a good dispersion efficiency of 97.2% after 0.5min settling time and 28.3% after 10min settling time to Bunker B oil with 10% water solution. Especially, the concentrated oil dispersant showing the low toxicity to Oryzias Latipes(24hr, TLm) was 54,000 ppm and to Brine Shrimp Artemia(24hr, TLm) was 51,000ppm, and also, it was completely biodegradated to 99.1% after 7~8days.

To prepare a O/W type durable softner(OESA), octadecamidoethylaminoethyl dodecate and tetra (2-dodecamidoethyl) urea synthesized as the main components of softner, were blended with polyoxyethylene(20) oleyl ether, sorbitan sesquioleate, and polyoxyethylene(7) stearyl ether in various compositions. Emulsion stability of OESA was good, and mixed HLB value was 9.7, OESA was found was to be good durable softner for nylon through the examination of softness, lubriation, antistatic property, bending resistance, and color fastness.

Oil dispersants using polyoxyethylene monooleate, polyoxyethylene oleylether, and poly(oxypropylene-oxyethylene)glycol block copolymer were prepared, and oil dispersant efficiency was measured using vertical shaking flask method to 4 kinds of Bunker B oil with different physical properties by appling the prepared dispersants. Although the dispersant efficiency was differed according to the differences of physical properties of Bunker B oil, the dispersant prepared using polyoxyethylene oleylether was the most effective to disperse the oil into water. The impurities like surfur contained in sample oil have to be removed by filteration to obtain the correct degree of absorption using UV spectrophotometer.