The introduction of natural dyes into modern dye houses is very promising green chemistry concept that should be popularized more to reduce the dependency of leather dyeing on some toxic and non-biodegradable synthetic dyes. In this study, the properties of dyeing of cochineal on cow leather were evaluated. The proper dyeing conditions were identified with dye uptake (K/S values) depending on the colorant concentration, dyeing duration, dyeing temperature, and dye bath pH. For the proper mordanting conditions, color changes for different mordants were observed as La*b* and H V/C values. Color fastness (light, rubbing, and dry cleaning) was also examined. Additionally, antibacterial properties and UV protection were examined. The results were as follows: The optimized dyeing conditions were 300% o.w.f., 40°C, 40 min., and pH 5. The cow leather color was red in the absence of mordanting, while it was red purple after being mordanted with Al and Cu, and purple mordanted with Fe. The K/S value of cow leathers increased in the order of the dyeing using AlK(SO4)2>CuSO4>FeSO4. The colorfastness to light and rubbing were reduced compared to original (untreated) cow leather. However dry cleaning fastness was very satisfactory, with a 4~5 rating. The dyed and pre-mordanting dyed cow leather showed excellent antibacterial properties.

Natural dye extracted from Salicornia bigelovii was applied to silk fabrics by dip dyeing process. The dyeing properties and the functionalities of the silk fabrics were determined. Factors affecting the dyeing properties such as dyestuff concentration, temperature, time and pH were studied. The colorimetric parameters L*, a*, b*, and H, V/C values were measured to select the optimal mordanting conditions. The colorfastnesses of the dyed and mordanted fabrics were estimated for practical use; in addition, the antibacterial property, ultraviolet protection properties were evaluated. The dyeabilities of silk increased depending on the increasing dye concentration, dyeing time, and dyeing temperature. And optimum dyeing results were achieved when dyeing with 300% (o.w.f.) of dye concentration at 90℃ for 100 minutes and at pH 3. The dyed silk fabrics without mordants produced yellow (Y) color and showed yellow (Y) or green yellow (GY) colors depending on the mordants type. The light fastness of dyed and Al mordanted silk fabrics were found to be excellent, and the drycleaning and rubbing fastness were good. The dyed silk fabrics showed no antibacterial property, but Al and Cu mordanted silk fabrics showed 99.9% reduction rate. The ultraviolet protection properties of the dyed silk fabric was improved. And the ultraviolet protection properties of mordanted samples showed very good ultraviolet protection properties.

In this study, the dyeing of silk fabric with Polygonum cuspidatum extracts was investigated. The contents of this study are as follows. First, the proper dyeing conditions were investigated by measuring the dye uptake (K/S value) that depended on the dyeing conditions when silk fabric was dyed with Polygonum cuspidatum extract. Second, the brightness (L), hue, and chroma differences that appear after mordanting with Al, Cu and Fe were investigated by measuring the CIELAB and Munsell values. And third, the colorfastness and antibacterial property were measured. When the silk fabric was dyed with Polygonum cuspidatum extract, the proper dyeing conditions were a colorant concentration of 90% v/v, a dyeing of time 100 minutes, a dyeing temperature of 70℃, and a dyeing of pH 3. In mordanting methods, the dyeabilities of post-mordanting were higher than those of premordanting. The hue value displayed yellow (Y) and yellow-red (YR) in cases of pre and post mordanting. The C value decreased by the mordanting of Polygonum cuspidatum extracts. Generally the colorfastness of mordanted fabrics was improved by mordanting. The dyed fabrics showed a 90.6% of Staphylococcus aureus reduction rate, and the dyed and mordanted fabrics showed 97.1% bacteria reduction rate. The dyed and mordanted fabrics showed above 90.5% Klebsiella pneumoniae reduction rate, and Cu mordant revealed the most effective bacterial reduction.

This study focuses on the effects of dyeing conditions and mordanting conditions, changes of colorfastness, antibacterial properties and UV protective of silk fabric dyed with Laminaria japonica extracts. A natural colorant was extracted from Laminaria japonica using distilled water as extractants. According to the results, maximum dye uptake (K/S) were obtained at 100% V/V colorant concentration, 80˚C, 60 min and pH 2. Silk fabric was dyed with Laminaria japonica extract at 80˚C for 60 min with pre-treatment or post-treatment of various metal salts as mordants. The Laminaria japonica extracts produced yellow hue on silk fabric in pre-mordanting and manifested green yellow hue mordanted with CuSO4 in post-mordanting method. Mordant CuSO4 for silk fabric was found to give good light fastness (rating 4). UV protection property did not increase significantly upon mordanting.

The fabric, 100% Silk, was dyed with Atractylodes japonica extract solution. The effects of concentration of extracts (colorant), temperature of dyeing, time of dyeing and pH of dye bath were studied. As the concentration of extracts increased, color strength (K/S value) increased progressively. The K/S values increased with raising temperature, time and proper conditions were 80℃ and 80 minutes. Maximum K/S value was obtained at pH 3. The K/S values of mordanted fabrics were increased with increasing mordant concentration up to specific values. Surface color of dyed and mordanted fabrics were yellowish. Light color fastness of fabric with mordanting was fairly good 3/4 rating. The mordanted silk fabrics showed excellent antibacterial activity. The silk fabric dyed with Atractylodes japonica extract showed a superior UV protective property.

The natural dyeing of silk fabric with Thuja orientalis extract was investigated. The proper colorant concentration, dyeing temperature, dyeing time, and pH for the dyeing of silk fabric with Thuja orientalis extract were 100% v/v, 80℃, 80 minutes and pH 3, respectively. In various mordanted methods, the K/S values of mordanted methods were higher than those of unmordanted methods with increasing mordant concentration. Light colorfastness and washing colorfastness of Cu or Fe mordanted silk fabric was improved by mordanting. The antibacterial properties of dyed and mordanted silk fabric showed a high reduction rate, and Thuja orientalis extract was showed effective bacterial reduction. The dyed and mordanted fabric with Thuja orientalis extract showed a superior ultraviolet protection property.