The study was done to change the morphology and pore size of SBA-15 silica, and the characteristics of SBA-15 silica were investigated with TG-DSC, XRD, SEM, TEM and N2 adsorption-desorption under changing aging conditions. SBA-15 silica having a 2D-hexagonal structure was synthesized and confirmed by SEM and TEM. The structure of mesoporus silica SBA-15 showed a pore having regularly formed hexagonal structure and a passage having a cylindrical shape. This result is in good agreement with the pore forming in XRD and cylindrical shape of the structure in N2 adsorption-desorption isotherm. SBA-15 silica showed a large BET surface area of 603-698 m2/g, a pore volume of 0.673-0.926 cm3/g, a large pore diameter of 5.62-7.42 nm, and a thick pore wall of 3.31-4.37 nm. This result shows that as the aging temperature increases, the BET surface area, pore volume, and pore diameter increase but the pore wall thickness decreases. The BET surface areas in SM-2 and SM-3 are as large as 698 m2/g. However, SM-2 has a large surface area and forms a thick pore wall, when the aging temperature is 100˚C and is synthesized into stable mesoporous SBA-15 silica.

균형대체모형은 시장에 대한 외생적인 충격의 효과를 분석하는데 매우 유용한 분석 모형이고 그러한 이유 때문에 정부정책에 대한 효과 분석에도 빈번하게 이용되어 왔다. 거의 대부분의 균형대체모형을 이용한 선행 연구가 완전경쟁적인 시장을 가정하였다는 사실은 많은 경험적인 연구가 가공식품 시장은 불완전 경쟁구조라는 사실을 보여주고 있다는 점에 비추어 볼 때 가공식품 시장에 적용하는 데는 그 모형상의 한계 또는 결과에 대한 해석상의 한계를 안고 있다고 해야 할 것이다. 이 논문은 가공식품 시장에 적용할 수 있는 과점시장 균형대체모형을 이론적으로 제시하고자 하였다. 과점시장에서는 완전경쟁시장과 달리 공급곡선이 존재하지 않지만, 적절한 가정이 수반된다면 과점시장의 균형을 분석할 수 있는 공급관계 곡선을 도출 할 수 있다. 이 논문이 기존의 과점시장 모형에 관한 연구에 기여한 점은 과점시장의 균형점에서 공급탄성치가 도출이 가능하다는 것을 보여준 것이며, 과점시장의 공급탄성치는 시장구조 파라미터와 수요탄성치로부터 독립해서 존재하지 않는다는 점을 입증한 것이다. 이 논문에서 균형대체모형을 통해 제시한 보조금정책 분석 방법은 조세정책에도 그대로 응용될 수 있으며, 가공식품 산업 이외에도 1차 산품을 가공하는 다른 산업에도 적용될 수 있을 뿐만 아니라 환경오염과 관련된 이슈에도 적용이 가능하다.