In this work, ultra-fine calcium oxide (CaO) powder derived from eggshells is used as the starting material to synthesize mineral trioxide aggregate (MTA). The prepared CaO powder is confirmed to have an average particle size of 500 nm. MTAs are synthesized with three types of fine CaO-based powders, namely, tricalcium silicate (C3S), dicalcium silicate (C2S), and tricalcium aluminate (C3A). The synthesis behavior of C3S, C2S and C3A with ultra-fine CaO powder and the effects of C3A content and curing time on the properties of MTA are investigated. The characteristics of the synthesized MTA powders are examined by X-ray diffraction (XRD), field emission-scanning electron microscope (FE-SEM), and a universal testing machine (UTM). The microstructure and compressive strength characteristics of the synthesized MTA powders are strongly dependent on the C3A wt.% and curing time. Furthermore, MTA with 5 wt.% C3A is found to increase the compressive strength and shorten the curing time.

WO3에 NiO를 첨가하여 제조한 후막형 시편의 미세구조와 전기적 성질에 대해 연구하였다. NiO 첨가에 따른 WO3의 결정립 성장이 억제되었고, 입도 분포도 균일하였으나 첨가량에 따른 결정립 크기 변화정도는 작았다. 산소 분압 감소로 WO3의 전도성은 증가하였고, NiO 첨가에 의해 고용한계 이하에서는 전도성이 증가하였고, 이상에서는 전도성이 감소하였다. 온도 증가에 따라 외인성 (extrinsic) 구간에서는 전도성 변화가 적었고, 고온의 진성 (intrinsic) 구간에서는 전도도가 급격히 증가하였으며, 이들의 중간 온도에서는 산소흡착에 따라 전도도가 감소하였다.