Insoluble catalytic electrodes were fabricated by RF magnetron sputtering of Pt on Ti substrates and the performance of seawater electrolysis was compared in these electrodes to that is DSA electrodes. The Pt-sputtered insoluble catalytic electrodes were nearly 150 nm-thick with a roughness of 0.18μm, which is 1/660 and 1/12 of these values for the DSA (dimensionally stable anodes) electrodes. The seawater electrolysis performance levels were determined through measurements of the NaOCl concentration, which was the main reaction product after electrolysis using artificial seawater. The NaOCl concentration after 2 h of electrolysis with artificial seawater, which has 3.5% NaCl normally, at current densities of 50, 80 and 140 mA/cm2 were 0.76%, 1.06%, and 2.03%, respectively. A higher current density applied through the electrodes led to higher electrolysis efficiency. The efficiency reached nearly 58% in the Pt-sputtered samples after 2 h of electrolysis. The reaction efficiency of DSA showed higher values than that of the Pt-sputtered insoluble catalytic electrodes. One plausible reason for this is the higher specific surface area of the DSA electrodes; the surface cracks of the DSAs resulted in a higher specific surface area and higher reaction sites. Upon the electrolysis process, some Mg- and Ca-hydroxides, which were minor components in the artificial seawater, were deposited onto the surface of the electrodes, resulting in an increase in the electrical resistances of the electrodes. However, the extent of the increase ranged from 4% to 7% within an electrolysis time of 720 h.

Most TCOs such as ITO, AZO(Al-doped ZnO), FTO(F-doped SnO2) etc., which have been widely used in LCD,touch panel, solar cell, and organic LEDs etc. as transparent electrode material reveal n-type conductivity. But in order to realizetransparent circuit, transparent p-n junction, and introduction of transparent p-type materials are prerequisite. Additionalprerequisite condition is optical transparency in visible spectral region. Oxide based materials usually have a wide optical band-gap more than ~3.0eV. In this study, single-phase transparent semiconductor of SrCu2O2, which shows p-type conductivity, havebeen synthesized by 2-step solid state reaction at 950oC under N2 atmosphere, and single-phase SrCu2O2 thin films of p-typeTCOs have been deposited by RF magnetron sputtering on alkali-free glass substrate from single-phase target at 500oC, 1%H2/(Ar+H2) atmosphere. 3% H2/(Ar+H2) resulted in formation of second phases. Hall measurements confirmed the p-typenature of the fabricated SrCu2O2 thin films. The electrical conductivity, mobility of carrier and carrier density 5.27×10−2S/cm,2.2cm2/Vs, 1.53×1017/cm3 a room temperature, respectively. Transmittance and optical band-gap of the SrCu2O2 thin filmsrevealed 62% at 550nm and 3.28eV. The electrical and optical properties of the obtained SrCu2O2 thin films deposited by RFmagnetron sputtering were compared with those deposited by PLD and e-beam.