This experiment can maximize the decline of the heat on steel structure by using the magnesium hydroxide and aluminum hydroxide which generally used to resistant or retardant. These materials can delay a temperature rise due to the generation of vapors around the fire resistive covering, when reacting with heat by a creating moisture. Therefore, applicability of the fire resistance mortar used magnesium hydroxide and aluminum hydroxide was studied and experimented. As a result, in case of the workability is satisfied with the condition of site, but in case of the bonding strength is not satisfied with the standard with fire resistance mortar.

Concrete indicates highly alkaline through hydration reaction of mortars that were attached to the RCA's surface. In this study, the carbonation of concrete incorporating coated RCA was investigated through accelerated carbonation test. As a results, coated RCA was indicated to be better than normal RCA.

Set-controlling admixtures via granulation method may be secured the operation time by adjusting the response time. therefore, mortar with Set-controlling admixtures via granulation is measured setting-time. As a result, the possibility of initial reaction control confirmed and also was developed the required properties of setting-time.

본 연구에서는 시멘트에 작용하는 아크릴 코폴리머의 화학반응을 통해 강한 점착성과 유연성을 가지는 친환경적인 폴리비닐아세테이트(PVAc)를 이용하여 수밀성을 향상시키는 복합공법의 가능성을 알아보고자 하였으며, 이를 위한 실험 방법으로 1차로 실리케아트계 침투성 방수제를 도포 한 후, 2차로 PVAc를 혼입한 모르타를 도포한 후에 부착강도 및 흡수량에 대한 특성을 검토하였다. 이 실험 결과를 토대로 하여 현장 적용을 위한 Mock-up 부재를 제작하였고, 이 시험 부재에 대하여 복합공법을 적용한 후 실내 시험과 동일한 성능을 검토하였다. 또한, 탄산화 및 염소 이온 침투저항성 평가를 실시하여 내구성이 취약한 환경에 적합한지 여부를 검토 하였다. 그 결과 PVAc를 이용한 복합공밥을 적용한 시험체가 수밀성능이 가장 우수하였으며, 부착강도 또한 우수한 성능을 나타내었다. 또한, 간이 Mock-up 부재에 대한 성능평가에서 실내 시험과 동일한 경향을 보였으며, 압축강도 시험결과 보강 효과를 발휘함을 알 수 있었다. 탄산화 및 염소 이온 침투저항성 내구 성능 평가에서 가장 우수한 결과를 나타내어 지하구조물 및 해양구조물 등과 같은 취약한 지역에 적용이 가능함을 확인 할 수 있었다.

Be constructed in the Middle East, recent overseas plant business mainly due to an increase in the amount of concrete in the construction sector is growing. When using plain concrete and concrete development of the initial expansion of the initial hydration, due to thermal stress that causes cracks in the concrete problems, and prevention of this by the use of the delay is expected to increase. In addition to the increase in domestic traffic produced in ready-mixed concrete plants and concrete due to high temperature during transportation upon arrival at the scene quickly if condensation begins to degrade due to the slump loss and workability after curing of cold joint and cause filling defects and the need for the measures . In the case of the powder that is currently on the market in order to obtain a uniform delay effects can be mixed, may be added, such as, wet, etc. Keep a less efficient storage, even if the delay has to be taken. This powder improves the delay and store it in a tablet, a delay effect to encourage the development of tablet, and the delay for compliance with basic properties was investigated.

본 연구에서는 폐콘크리트에서 발생하는 순환잔골재가 구조용 재료로서 많은 문제점이 있음을 인지하고 순환잔골재가 포함하고 있는 미분말이 강도증진 효과와 유동성을 증가 시킬 수 있다는 특성을 이용하여 자기충전 콘크리트(Self-Compacting Concrete, 이하 SCC로 표기)에 활용하게 되었다. 즉 순환잔골재가 갖는 미분말이 자기충전 콘크리트 특성인 고강도(40 MPa 이상)와 높은 유동성(JSCE 2등급)을 발현하기에 적당하여 폐콘크리트에서 발생하는 순환잔골재를 일반잔골재 대비 순환잔골재의 혼입률을 25%씩 증가시켜, 총 5수준으로 달리하여 자기충전 콘크리트에 적용하였으며, 이에 따라 굳지 않은 콘크리트의 물리적 특성, 경화한 콘크리트의 역학적 및 내구 특성을 검토하여 순환잔골재를 자기충전 콘크리트 재료로서 활용 가능성을 검토하고자 한다. 그 결과 물리적, 역학적 및 내구특성의 5수준 배합비율 중 일반잔골재 대비 순환잔골재는 50% 혼입률까지 적용 가능하다는 결론을 얻었으며, 그 이상의 혼입률에서는 오히려 성능저하가 발생한다는 것을 알 수 있었다. 또한 실생활에서의 적용 가능성을 알아보기 위한 실구조물의 적용성이 차후 검토 되어야 할 것으로 판단된다.