Changes in surface morphology and roughness of dc sputtered ZnO:Al/Ag back reflectors by varying the deposition temperature and their influence on the performance of flexible silicon thin film solar cells were systematically investigated. By increasing the deposition temperature from 25˚C to 500˚C, the grain size of Ag thin films increased from 100 nm to 1000 nm and the grain size distribution became irregular, which resulted in an increment of surface roughness from 6.6 nm to 46.6 nm. Even after the 100 nm thick ZnO:Al film deposition, the surface morphology and roughness of the ZnO:Al/Ag double structured back reflectors were the same as those of the Ag layers, meaning that the ZnO:Al films were deposited conformally on the Ag films without unnecessary changes in the surfacefeatures. The diffused reflectance of the back reflectors improved significantly with the increasing grain size and surface roughness of the Ag films, and in particular, an enhanced diffused reflectance in the long wavelength over 800 nm was observed in the Ag back reflectors deposited at 500˚C, which had an irregular grain size distribution of 200-1000 nm and large surface roughness. The improved light scattering properties on the rough ZnO:Al/Ag back reflector surfaces led to an increase of light trapping in the solar cells, and this resulted in a noticeable improvement in the Jsc values from 9.94 mA/cm2 for the flat Ag back reflector at 25˚C to 13.36 mA/cm2 for the rough one at 500˚C. A conversion efficiency of 7.60% (Voc = 0.93, Jsc = 13.36 mA/cm2, FF = 61%) was achieved in the flexible silicon thin film solar cells at this moment.

This paper investigates the dependence of a-Si:H/c-Si passivation and heterojunction solar cell performances on various cleaning processes of silicon wafers. It is observed that the passivation quality of a-Si:H thin-films on c-Si wafers depends highly on the initial H-termination properties of the wafer surface. The effective minority carrier lifetime (MCLT) of highly H-terminated wafer is beneficial for obtaining high quality passivation of a-Si:H/c-Si. The wafers passivated by p(n)-doped a-Si:H layers have low MCLT regardless of the initial H-termination quality. On the other hand, the MCLT of wafers incorporating intrinsic (i) a-Si:H as a passivation layer shows sensitive variation with initial cleaning and H-termination schemes. By applying the improved cleaning processes, we can obtain an MCLT of 100μsec after H-termination and above 600μsec after i a-Si:H thin film deposition. By adapting improved cleaning processes and by improving passivation and doped layers, we can fabricate a-Si:H/c-Si heterojunction solar cells with an active area conversion efficiency of 18.42%, which cells have an open circuit voltage of 0.670V, short circuit current of 37.31 mA/cm2 and fill factor of 0.7374. These cells show more than 20% pseudo efficiency measured by Suns-Voc with an elimination of series resistance.

Changes in the surface morphology and light scattering of textured Al doped ZnO thin films on glasssubstrates prepared by rf magnetron sputtering were investigated. As-deposited ZnO:Al films show a hightransmittance of above 80% in the visible range and a low electrical resistivity of 4.5×10-4Ω·cm. The surfacemorphology of textured ZnO:Al films are closely dependent on the deposition parameters of heater temperature,working pressure, and etching time in the etching process. The optimized surface morphology with a cratershape is obtained at a heater temperature of 350oC, working pressure of 0.5 mtorr, and etching time of 45seconds. The optical properties of light transmittance, haze, and angular distribution function (ADF) aresignificantly affected by the resulting surface morphologies of textured films. The film surfaces, havinguniformly size-distributed craters, represent good light scattering properties of high haze and ADF values.Compared with commercial Asahi U (SnO2:F) substrates, the suitability of textured ZnO:Al films as frontelectrode material for amorphous silicon thin film solar cells is also estimated with respect to electrical andoptical properties.