In this study, the performance of the self-healing with the granulated alkali activator (Ca(OH)2) manufactured in seawater environment is investigated for crack healing under 300 μm of cracks. Specimens combined with GGBFS and OPC with and without the granulated alkali activator were manufactured and immersed in seawater. After that, crack recovery on the surface of the specimens with the granulated alkali activator (Ca(OH)2) was also evaluated by the ultrasonic pulse velocity test. From the results, it was verified that cementitious materials with the granulated alkali activator, exposed in marine environments, could be able to heal or seal inside cracks

In this study, Retarder, which shows characteristics of delay hydration reaction and reduce hydration heat in concrete, was processed through granulation and paraffin coat to induce reation by hydration heat. Concrete with Granulated and paraffin coated retarder were prepared and compressive strength was measured by curing at 20℃ and 40℃. As a result, it was confirmed that retarder exhibits performance depending on the curing temperature.

In this study, Retarder, which shows characteristics of delay hydration reaction and reduce hydration heat in concrete, was processed through granulation and paraffin coat to induce reation by hydration heat. Concrete with Granulated and paraffin coated retarder were prepared and compressive strength was measured by curing at 20℃ and 40℃. As a result, it was confirmed that retarder exhibits performance depending on the curing temperature.