The effects of an excess of Bi on the piezoelectric and dielectric properties of 0.60Bi1+xFeO3-0.40BaTiO3 (x = 0, 0.01, 0.03, 0.05, 0.07) were investigated. The ceramics were processed through a conventional solid state reaction method and then quenched after sintering at different temperatures in the range of 980~1070 oC. A single perovskite structure without any secondary phase was confirmed for all compositions and temperatures. It was found that excess Bi reduced the sintering temperatures, acted as a sintering aid and enhanced the properties in combination with quenching. Curie temperature (TC) was found to slightly increase due to the presence of excess Bi; electrical properties were also improved by quenching. At x = 0.03 and 1030 oC, remnant polarization (2Pr) was as high as 45.4 μC/cm2 and strain at 40 kV/cm was up to 0.176 %.

외국으로부터 수집한 당과작물의 생육특성을 조사하여 생물에너지 자원으로 이용 가능성을 검토하고자 1986～1988년에 걸쳐 경남 진주에서 실시한 시험결과는 다음과 같다. 1. 단수수는 1988년 5월 20일 파종에서 공시품종들의 파종으로부터 출수까지의 일수는 70～l18일 이었다. 경의 당도는 6.0～l4.0%이었고, 생체중은 10a당 4～15t이었다. s-1은 재배기간 2회까지 예취가 가능하였다. 2. 사탕무는 수확까지 생엽을 유지하였고, 근중은 3.542～6,397kg/10a이었으며, 근의 당도는 9.2 ～ 19.8%이었다 3. 사방수수는 10월하순까지 생장을 계속하였고, 그 후는 생장이 정지되었다. 경의 당도는 13.2 ～ 16.1%이었다 4. 단수수의 파종기별 생육량은 조파할수록 많았고, 경의 당도도 높았다 5. 단수수의 착즙액으로 부터 alcohol 수득량은 10a당 186 까지 얻을 수 있었다.