BiFeO3 with perovskite structure is a well-known material that has both ferroelectric and antiferromagnetic properties called multiferroics. However, leaky electrical properties and difficulty of controlling stoichiometry due to Bi volatility and difficulty of obtaining high relative density due to high dependency on the ceramic process are issues for BiFeO3 applications. In this work we investigated the sintering behavior of samples with different stoichiometries and sintering conditions. To understand the optimum sintering conditions, nonstoichiometric Bi1±xFeO3±δ ceramics and Ti-doped Bi1.03Fe1-4x/3TixO3 ceramics were synthesized by a conventional solid-state route. Dense single phase BiFeO3 ceramics were successfully fabricated using a two-step sintering and quenching process. The effects of Bi volatility on microstructure were determined by Bi-excess and Ti doping. Bi-excess increased grain size, and Ti doping increased sintering temperature and decreased grain size. It should be noted that Ti-doping suppressed Bi volatility and stabilized the BiFeO3 phase.

방울토마토는 냉·한대 지역을 제외하고는 세계적으로 생산 및 소비되는 채소로 수확 후 품질관리 등에 대한 연구가 많이 이루어지고 있다. 본 연구에서는 비파괴 측정 방법들 중 하나인 자기공명영상(Magnetic Resonance Imaging, MRI)기술을 활용하여 방울토마토의 품종 및 성숙단계별 과실 내부 구조의 변화를 비교하였다. 공시재료는 방울토마토 3품종(티아라, 티아라_TY, 유니콘)에 대하여 성숙단계를 과피색을 기준으로 6단계로 세분화하고 3반복으로 MRI 영상을 획득하였다. 실험은 전북대학교 부설 농업기계 ICT 융합 연구소가 보유하고 있는 MRI 시스템을 활용하여 이미지를 얻었다. 자기공명영상 이미지는 Gradient Echo 펄스열을 사용하였고, 횡단면(Axial)의 영상면(Image Direction)을 중심으로 영상영역(Field of View, FOV)은 50 mm x 50 mm로 1회 촬영할 때마다 20개의 영상들을 얻었다. 촬영하여 얻은 영상들과 직접적으로 비교하기 위해 영상면과 같은 방향으로 임의적으로 방울토마토의 중간을 칼로 잘라 비교하였다. 촬영과 실제 잘라 내부를 비교해본 결과, 방울토마토 내부 심실의 수는 다른 품종들에 비해 티아라 품종이 가장 많았다. 생육단계별로는 3품종 모두 마지막 단계(Red Stage)의 중과피의 형태가 뚜렷하게 구분되지 않았으며, 특히 유니콘품종의 경우 다른 품종들에 비해 더 빠르게 모호해지는 것을 알 수 있었다. 또한 유니콘 품종의 경우, 다른 두 품종에 비해 미숙단계인 1,2단계(Green Stage, Breaker Stage)에서 중과피의 형태가 빠르게 발달하는 것이 확인되었다. 본 연구를 통하여, 방울토마토와 같이 성숙단계별 내부 변화가 크게 일어나는 과실에 대하여 비파괴 자기공명영상으로 분석함으로써 재배 환경조건에 따른 품종별 내부 생리장해 및 형태의 신속한 변화 탐지에 효율적으로 활용될 수 있는 가능성을 확인하였다.

경상북도에 위치한 유전자원보호구역 3개 지역( 봉화지역의 자작나무, 영주지역의 신갈나무, 울진지역의 소나무)을 식생 유형에 따라 2016년 5월에서 9월까지 함정 트랩(pitfall trap)을 5회씩 3반복하여 각각 상대적으로 비교하였다. 채집된 보행성 딱정벌레류는 딱정벌레과 등 총 25과 116종 1,663개체가 확인되었으며 자작나무 군락에서 종풍부도(72), 종균등도(0.829), 종다양도(3.544) 모두 가장 높게 나타났다. MRPP(Multi-response Permutation procedures)분석결과 서식지에 대한 군집차이가 있다고 확인되었으며(p < 0.001), Bray-curtis 분석결과 군집간의 확연한 차이와 함께 자작나무 군락이 보행성 딱정벌레류의 종 풍부도에 큰 영향을 주는 것으로 나타났고 소나무군락은 다른 지역과 비교해 상대적으로 낮은 영향을 받았다. 식생 유형에 대한 지표종 분석결과 자작나무군락에서 끝무늬녹색먼지벌레 (Chlaenius micans Fabricius)를 포함한 4종, 신갈나무 지역에서 긴윤머리먼지벌레(Trichotichnus coruceus Tschitscherine) 를 포함한 9종, 소나무 지역에서 솔곰보바구미(Hylobius harodi Faust)를 포함한 3종의 지표종이 확인되었다.

The effects of an excess of Bi on the piezoelectric and dielectric properties of 0.60Bi1+xFeO3-0.40BaTiO3 (x = 0, 0.01, 0.03, 0.05, 0.07) were investigated. The ceramics were processed through a conventional solid state reaction method and then quenched after sintering at different temperatures in the range of 980~1070 oC. A single perovskite structure without any secondary phase was confirmed for all compositions and temperatures. It was found that excess Bi reduced the sintering temperatures, acted as a sintering aid and enhanced the properties in combination with quenching. Curie temperature (TC) was found to slightly increase due to the presence of excess Bi; electrical properties were also improved by quenching. At x = 0.03 and 1030 oC, remnant polarization (2Pr) was as high as 45.4 μC/cm2 and strain at 40 kV/cm was up to 0.176 %.

This paper is about improvements to prevent the crack on welding parts of bleed air duct and vent tube in Advanced Trainer ECS owing to vibration. The configurations and the path of vent tube should be changed to prevent the crack. To assure the result of improvements, measured the status of each pressure condition attaching pressure censers on duct and vent tube. The result of life analysis shows that a crack does not happen on improved configuration while a crack initiates after 19th flight and thru cracking could happen after the 30th flight on previous configuration.

본 조사를 통하여 2015년 6월부터 8월까지 태안군에서 13개 지역을 선정하여 곤충상을 조사 하였다. 주요조사방법으로 임도와 등산로, 생태탐방로를 따라 포충망을 이용한 채어잡기와 쓸어잡기 방법으로 주간 채집을 실시하였고, UV light trap을 이용한 야간 채집을 수행하였다. 채집된 육상곤충은 총 12목 77과 491종 3657개체가 확인되었고, 이 중 고유종으로 줄우단풍뎅이 (Gastroserica herzi Heyden, 1887, 딱정벌레목 : 검정풍뎅이과), 우리벼밤나방 (Sesamia pseudoturpis Kononenko et Ahn, 1998, 나비목 : 밤나방과), 제일줄나비 (Limenitis helmanni Lederer, 1853, 나비목 : 네발나비과), 팔공산밑들이메뚜기 (Anapodisma beybienkoi Rentz et Miller, 1971, 메뚜기목 : 메뚜기과)와 기후변화생물지표종 먹그림나비 (Dichorragia nesimachus Boisduval, 1836, 나비목 : 네발나비과), 암끝검은표범나비 (Argyreus hyperbius Linnaeus, 1763 나비목 : 네발나비과), 제주등줄박 각시 (Marumba spectabilis Okamoto, 1924, 나비목 : 박각시과)가 확인되었다. Shannon’s diversity 지수(H)와 Simpon’s diversity 지수(D′)를 이용하여 각 지역별 다양성을 산출하였는데 안면도 휴양림 (H=4.486, D′=0.9804)이 가장 높게 나타났으며, 대소산 (H=4.175, D′=0.9622)이 다음으로 높은 다양성을 보였다. 주성분분석(Principal Component Analysis) 결과 월별 종 구성의 차이는 크게 나타나지 않았지만, 지역별 구성에서 백화산, 안면도 휴양림, 대소산에서 다른 군집과 매우 상이한 종 구성을 보였다.

TiAlN films were deposited on WC-5Co substrates with different buffer layers by D.C. magnetron sputtering. The films were evaluated by microstructural observations and measuring of preferred orientation, hardness value, and adhesion force. As a process variable, various buffer layers were used such as TiAlN single layer, TiAlN/TiAl, TiAlN/TiN and TiAlN/CrN. TiAlN coating layer showed columnar structures which grew up at a right angle to the substrates. The thickness of the TiAlN coating layer was about 1.8μm, which was formed for 200 minutes at 300˚. XRD analysis showed that the preferred orientation of TiAlN layer with TiN buffer layer was (111) and (200), and the specimens of TiAlN/TiAl, TiAlN/CrN, TiAlN single layer have preferred orientation of (111), respectively. TiAlN single layer and TiAlN/TiAl showed good adhesion properties, showing an over 80N adhesion force, while TiAlN/TiN film showed approximately 13N and the TiAlN/CrN was the worst case, in which the layer was destroyed because of high internal residual stress. The value of micro vickers hardness of the TiAlN single layer, TiAlN/TiAl and TiAlN/TiN layers were 2711, 2548 and 2461 Hv, respectively.

Experiment on the thermal response of college-age Korean was conducted in a thermal environmental chamber during winter season. Eight environmental conditions composed of five air temperatures (18∼26℃) and two relative humidities (40, 60%) were selected. To investigate the uniformity of thermal environments, the spatial distributions and the temporal variations of thermal parameters were examined in the test chamber. Subjects of 7 females or 7 males were questioned in the chamber for three hours, where thermal and comfort sensations were surveyed every fifteen minutes. The repeatability and temporal variation of thermal response were discussed. The thermal sensation votes of subjects were compared with the predicted mean votes calculated from the thermal parameters and human parameters. The correlation between thermal sensation votes and comfort sensation votes of subjects were discussed.