The effect of use of as PCA(process control agent) to prevent the carbon contamination during mechanical alloying process and the precipitation behavior in Ni-20Cr-20Fe-5Nb bulk alloy after aging were investigated. NbC and were formed during mechanical alloying and consolidation processes in the Ni-20Cr-20Fe-5Nb alloy in which methanol() was added as PCA. Formation of NbC in this alloy decreased the amount of Nb dissolved in the Ni matrix. The use of as PCA in Ni-20Cr-20Fe-5Nb alloy prevented the formation of NbC and increased the hardness. The increase of hardness in this alloy was attributed to the increased amount of Nb dissolved in the Ni matrix. After aging treatment for 20 hours at of Ni-20Cr-20Fe-5Nb bulk alloy in which added as PCA, precipitates were formed, respectively. The precipitation temperatures of and in this bulk alloy were lower than those in commercial IN 718 alloy. It seemed that the lower precipitation temperatures for and in this bulk alloy than in commercial IN 718 alloy were due to severe plastic deformation during mechanical alloying.

고속도 공구강 기판에 반응성 스퍼터링법으로 증착된 HfN/Si3N4와 NbN/Si3N4다층박막의 기계적인 성질들을 막 증착 조건에 따라 평가하였다. HfN/Si3N4와 NbN/Si3N4 다층박막의 강도는 N2/Ar비가 0.4일 때가지 증가하다가 유량비가 증가함에 따라 더 이상 증가하지 않았다. 두 다층박막의 강도는 낮은 온도에서의 열처리에 의해서는 거의 변화가 업지만 800˚C 정도의 고온에서는 열처리에 의한 산화로 인하여 감소하였다. 낮은 온도에서의 열처리는 밀착성을 향상시키는 반면 고온에서의 열처리는 강도의 감소 이외에 밀착성이 감소하므로 바람직하지 못하다.

원소 분말을 합성하여 Ti5SI3 화합물을 합성하는 방법을 연구하였다. 합성법으로서는 기본적으로 반응소결법을 사용하였으며, 치밀화를 위하여는 유사-열간 정수압 성형법(PHIP, pseude-hot isostatic pressing)을 사용하였다. 반응소결법에서는 분말의 입도, 반응온도 및 유지시간이 소결밀도에 영향을 주었으며, PHIP법에 의한 치밀화에서는 압력 및 유지 간이 주요 변수로 사용되었다. 이들 변수중 미세한 입도와 유지시간이 기공을 감소시켰다. 또한 Cu의 첨가 영향을 연구하였는데, 약 6wt%이내의 Cu 첨가는 밀도 향상에 좋은 영향을 미쳤다. 반응소결 및 PHIP를 통해 Ti5SI3 -Cu의 상대밀도를 약 99%까지 높일 수 있었으며, 이때 Cu의 효과는 감도지수 부합됨을 확인하였다.