The processes for the preparation of ZnO powder by using EAF(electric arc furnace)dust was studied by wetting method which are divided to two steps, carried out of the elution processes by various concentrations of sulfuric acid is reacted with EAF dust as the former, and the latter were performed by a number of specified processes, which are leaching process depends on various pH, cementation, ozone and heat treatment processes etc. Experimental results showed that the appropriate pH range is pH7.5~8.0 and the resulting zinc content is range of 37~38%, the residual quantities of the heavy metals are less than 3ppm individually by cementation process except Mn, even though the Mn metal could not be removed by cementation process but was removed up to 0.2ppm by the ozone process from 70ppm initially. Finally, 80.2% of ZnO was obtained by the heat treatment at 500℃.

Elution effect was studied by the reactions between Electric arc furnace(EAF)dust and conc. or dil. sulfuric acid for the purpose of recoverying of the useful metals afterwards. The methods of mixing with acids and EAF dust for the elutions were depend on the ratios of acid/EAF dust. Experimental results showed that increased the ratios of sulfuric acids, decreased the elution effects are on the Zn, Fe and Mn, and conc. sulfuric acid showed higher elution effects than dil. sulfuric acids for the all metals. But in case of Pb, dil. sulfuric acid showed higher elution effects than conc. sulfuric acids conversely. Furthermore, the reason of the extreamly low quantities of eluted Pb is caused by the low solubilities by sulfuric acids compared to the other metals, as the results of the insoluble Pb is removed by the process of filtering.

EAF dust which is contained around 30% of zinc, 15% of iron and 3% of lead individually, is chemically treated by ammonium chloride, ammonia water, ammonia gas and carbon dioxide, and also tested and identified the ratios of the recovery of In by applied the variations of particle size, pH and heating temperature as well, in order to getting optimized recovery of the In metal after performing all of those processes. Experimental results showed that the rate of Zn recovery is 97% when the mixture of 1.3 of NH4Cl/EAF is heated to the temperature of 400℃ and leached by water, and 95% recovery of In when ammonia gas and carbon dioxide is added simultaneously and adjust the 9.5 of pH to the same mixture above. For the purpose of remove the impurities in the mixed sample, which is prepared by the two samples, indicated above showing as the ratio of 95% and 97% recovery, in case of applied the cementation process to it, and also by electrolytic process, produced the In plate of 95~97%, and acquired 99-99.5% of In metal ingot finally by applied the heating process at 470~500℃.