The recycling of solid waste materials to fabricate carbon-based electrode materials is of great interest for low-cost green supercapacitors. In this study, porous carbon foam (PCF) was prepared from waste floral foam (WFF) as an electrode material for supercapacitors. WFF was directly carbonized at various temperatures of 600, 800, and 1,000 oC under an inert atmosphere. The WFF-derived PCF (C-WFF) was found to have a specific surface area of 458.99 m2/g with multi-modal pore structures. The supercapacitive behavior of the prepared C-WFF was evaluated using a three-electrode system in a 6 M KOH aqueous electrolyte. As a result, the prepared C-WFF as an active material showed a high specific capacitance of 206 F/g at 1 A/g, a rate capability of 36.4 % at 20 A/g, a specific power density of 2,500 W/kg at an energy density of 2.68 Wh/kg, and a cycle stability of 99.96 % at 20 A/g after 10,000 cycles. These results indicate that the C-WFF prepared from WFF could be a promising candidate as an electrode material for high-performance green supercapacitors.

In this study, N/S co-doped carbon felt (N/S-CF) was prepared and characterized as an electrode material for electric double-layer capacitors (EDLCs). A commercial carbon felt (CF) was immersed in an aqueous solution of thiourea and then thermally treated at 800 oC under an inert atmosphere. The prepared N/S-CF showed a large specific surface area with hierarchical pore structures. The electrochemical performance of the N/S-CF-based electrode was evaluated using both 3- electrode and 2-electrode systems. In the 3-electrode system, the N/S-CF-based electrode showed a good specific capacitance of 177 F/g at 1 A/g and a good rate capability of 41% at 20 A/g. In the 2-electrode system (symmetric capacitor), the freestanding N/S-CF-based electrode showed a specific capacitance of 275 mF/cm2 at 2 mA/cm2, a rate capability of 62.5 % at 100 mA/cm2, a specific power density of ~ 25,000 mW/cm2 at an energy density of 23.9 mWh/cm2, and a cycling stability of ~ 100 % at 100 mA/cm2 after 20,000 cycles. These results indicate the N/S co-doped carbon felts can be a promising candidate as a new electrode material in a symmetric capacitor.

Hierarchically porous carbon materials with high nitrogen functionalities are extensively studied as highperformance supercapacitor electrode materials. In this study, nitrogen-doped porous carbon textile (N-PCT) with hierarchical pore structures is prepared as an electrode material for supercapacitors from a waste cotton T-shirt (WCT). Porous carbon textile (PCT) is first prepared from WCT by two-step heat treatment of stabilization and carbonization. The PCT is then nitrogendoped with urea at various concentrations. The obtained N-PCT is found to have multi-modal pore structures with a high specific surface area of 1,299 m2 g−1 and large total pore volume of 1.01 cm3 g−1. The N-PCT-based electrode shows excellent electrochemical performance in a 3-electrode system, such as a specific capacitance of 235 F g−1 at 1 A g−1, excellent cycling stability of 100 % at 5 A g−1 after 1,000 cycles, and a power density of 2,500 W kg−1 at an energy density of 3.593 Wh kg−1. Thus, the prepared N-PCT can be used as an electrode material for supercapacitors.

Porous carbons have been widely used as electrode material for supercapacitors. However, commercial porous carbons, such as activated carbons, have low electrochemical performance. Nitrogen-doping is one of the most promising strategies to improve electrochemical performance of porous carbons. In this study, nitrogen self-doped porous carbon (NPC) is prepared from melamine foam by carbonization to improve the supercapacitive performance. The prepared NPC is characterized in terms of the chemical structures and elements, morphology, pore structures, and electrochemical performance. The results of the N2 physisorption measurement, X-ray diffraction, and Raman analyses reveal that the prepared NPC has bimodal pore structures and pseudo-graphite structures with nitrogen functionality. The NPC-based electrode exhibits a gravimetric capacitance of 153 F g−1 at 1 A g−1, a rate capability of 73.2 % at 10 A g−1, and an outstanding cycling ability of 97.85% after 10,000 cycles at 10 A g−1. Thus, the NPC prepared in this study can be applied as electrode material for high-performance supercapacitors.

상업적으로 이용되는 폴리스티렌계 이온교환막은 제조 공정이 쉽고 간단하지만 막이 가지는 취성 때문에 내구성이 약하다는 단점을 가지고 있다. 이를 보완하기 위하여 친수성 그룹인 poly(ethylene glycol)을 곁사슬로 가지고 있는 poly(ethylene glycol)methyl ether methacrylate를 공중합시켜 음이온 교환막을 합성하였다. 지지체로는 내화학성 및 기계적 강도가 우수한 다 공성 PE 지지체를 사용하였고, 여기에 다양한 조성의 vinylbenzyl chloride, styrene, poly(ethylene glycol)methyl ether methacrylate, divinylbenzene, benzoyl peroxide를 녹인 단량체 용액을 지지체 기공에 채운 뒤 열중합 가교시켜 trimethylamine을 이 용하여 음이온 교환기를 도입해 세공충전 음이온 교환막을 합성하였다. 또한 poly(ethylene glycol)methyl ether methacrylate의 곁사슬 길이와 각 단량체가 차지하는 비율의 변화가 음이온 교환막의 전기화학적 특성에 미치는 영향을 알아보았다.