방사선물질의 수송 및 저장용기 등에 사용되는 에폭시수지계 중섣자 차폐재, KNS-201, KNS-301 및 KNS-601을 제조하였다. 기본물질은 개질 및 수소 첨가된 비스페놀 A형 그리고 노블락형 에폭시수지이며, 첨가제로는 수산화알루미늄 및 탄화붕소이다. 이들 중성자 차폐재들의 열적 및 역학적 성질 및 재방사선성 등을 평가하기 위해 여러 특성시험을 행하였다. 조사된 제반 특성들은 열분해온도;257~280˚C, 열전도도;0.95~1.14W/m.K, 열팽창계수 ;0.77~1.26x10-6˚C-1, 연소특성;800˚C이하, 평균연소시간;5초 이하, 평균연소길이 ;5mm 이하, 인장강도;2.5~3.2Kg/mm2,압축강도:13.2~15.2kg/mm2 굴곡강도:5.2~604Kg/mm2 등을 나타냈다. 전반적으로 개발된 중성자 차폐재들의 관련 특성들이 외국에서 사용되는 중성자 차폐재, NS-4-RF보다 우수한 것으로 나타났다. 또한 KNS-601의 내방사선성이 KNS-201과 KNS-301보다 우수한 것으로 나타났다. 또한 KNS-601의 내방사선이 KNS-201과 KNS-301보다 우수한 것으로 나타났다.

A new process using rapid solidification (melt spinning method) followed by pressing and sintering was investigated to produce the n-type thermoelectric ribbons of 90% +10% doped with . Quenched ribbons are very brittle and consisted of homogeneous pseudo-binary solid solutions. Property variations of the materials was investigated as a function of variables, such as dopant quantity and sintering temperature. When the process parameters were optimized, the maximum figure of merit was .

The efficiency of thermoelectric devices for different applications is known to depend on the thermoelectric effectiveness of the material which tends to grow with the increase of its chemical homogeneity. Thus an important goal for thermal devices is to obtain chemically homogeneous solid solutions. In this work, the new process with rapid solidification (melt spinning method) followed by hot pressing was investigated to produce homogeneous material. Characteristics of the material were examined with HRD, SEM, EPMA-line scan and bending test. Property variations of the materials were investigated as a function of variables, such as dopant quantity and hot pressing temperature. Quenched ribbons are very brittle and consist of homogeneous , solid solutions. When the process parameters were optimized, the maximum figure of merit was 2.038×10-3K-4. The bending strength of the material hot pressed at 50 was 8.2 kgf/.

solid solutions are of great interest as materials for thermoelectric energy conversion. One of the key technologies to ensure the efficiency of thermoelectric device is to obtain chemically homogeneous solid solutions. In this work, the new process with rapid solidification followed by hot pressing was investigated to produce homogeneous thermoelectric materials. Characteristics of the materials were examined with XRD, SEM, EPMA-line scan and bending test. Property variations of the materials were investigated as a function of variables, such as excess Te quantity and hot pressing temperature. Quenched ribbons are very brittle and consisted of homogeneous , solid solutions. When the process parameters were optimized, the maximum figure of merit was 3.073. The bending strength of the material, hot pressed at 45, was 5.87 kgf/.