The ultrasonic method is an alternative to the conventional route to produce structured carbon materials, offering the advantages of synthesis in a short period of time under room temperature. The main objective of this work is to synthesize a sulfonated mesoporous carbon catalyst from a phenolic resin composed of phloroglucinol and formaldehyde. The synthesis was performed by the soft-template method in an ultrasonic processor and the product was subsequently carbonized and sulfonated for application in the esterification model reaction. Functionalization with sulfuric acid of MCS5-6 h sample brought about a decrease in porosity but simultaneously resulted in the generation of functional groups of an acidic nature. The MCS5-6 h catalyst with a sulfonic density of 1.6 mmol g− 1, surface area of 402 m2 g− 1 and pore diameter of 10.6 nm maintained in mesoporous even after acid treatment. MCS5-6 h showed excellent activity in the esterification reaction with 95% oleic acid conversion. The recyclability of MCS5-6 h was satisfactory during five reaction cycles. The present work addressed a promising alternative for the synthesis of carbon catalysts using ultrasound irradiation, thus providing an alternative with a lower cost of time and energy for large-scale production.

The perovskite- type oxide containing transition metals on the B-site show mixed (electronic/ionic) conductivity. These mixed-conductivity oxides are promising materials for oxygen permeating membranes. The main objective of this research work is to synthesize and characterization ceramic powders of the Sr-Co-Fe-O system for methane conversion using membrane reactor. SCFO powders were synthesized from the route was based on the complex method of combination of acid EDTA and citrate and shown be available by control efficient of synthesis to performed , moreover, it presented easy implementation, reproducibility and operation. Powder ceramic was characterized by XRD, microscopic optic, SEM and TG-DTA.

The present study investigates the behavior of the sintering and hardness of stainless steel samples reinforced with NbC and TaC. Matrixes of pure stainless steel were compacted with addition of up to 3% wt NbC or TaC in a cylindrical die of steel at 700 MPa and sintered in an electrical resistance furnace under argon atmosphere. The sintered samples were characterized by density and hardness measurement, optical microscopy and scanning electron microscopy (SEM). The preliminary results show that the size and distribution of carbides influence in the sintering and hardness of the sintered samples.