In the current steel structures of high-rise buildings, high heat input welding techniques are used to improve productivity in the construction industry. Under the high heat input welding, however, the microstructures of the weld metal (WM) and heat-affected zone (HAZ) coarsen, resulting in the deterioration of impact toughness. This study focuses mainly on the effects of fine TiN precipitates dispersed in steel plates and B addition in welding materials on grain refinement of the HAZ microstructure under submerged arc welding (SAW) with a high heat input of 200 kJ/cm. The study reveals that, different from that in conventional steel, the γ grain coarsening is notably retarded in the coarse grain HAZ (CGHAZ) of a newly developed steel with TiN precipitates below 70 nm in size even under the high heat input welding, and the refinement of HAZ microstructure is confirmed to have improved impact toughness. Furthermore, energy dispersive spectroscopy (EDS) and secondary-ion mass spectrometry (SIMS) analyses demonstrate that B is was identified at the interface of TiN in CGHAZ. It is likely that B atoms in the WM are diffused to CGHAZ and are segregated at the outer part of undissolved TiN, which contributes partly to a further grain refinement, and consequently, improved mechanical properties are achieved.

콩의 건물축적과 단백질전류에 대한 Source-Sink변경의 효과를 구명하기 위하여 1992년에 고려대학교 자연자원대학 실험농장에서 황금콩을 공시품종으로 착협시기(R3)에 상위 40%, 하위 60%의 엽과 협을 제거하여 건물중 및 단백질함량의 변화를 조사한 결과는 다음과 같다. 1. 상엽-하협제거처리에서 하위 엽과 경 건물중이 증가하였고, 상위 종실과 협 건물중은 감소하였다. 2. 엽의 단백질함량은 상위 엽보다 하위 엽에서 높았다. 3. 종실의 단백질함량은 상엽-하협제거와 하엽-상협제거처리에서 낮았다. 4. 상엽-하협제거처리에서 엽의 단백질함량은 가장 높았고 종실 단백질함량은 가장 낮았다. 5. 본 실험의 결과에서 콩의 단백질원은 하부에서 상부로 이동하나 생식생장기간중의 장거리 전류를 위한 엽 단백질의 재이동은 약한 것으로 나타났다.