The property changes of 18, 14, and 8K green gold alloys for jewelry are observed by adding 0.0, 3.0, and 5.0 wt% of indium (In), respectively. To check the composition of the alloys, an energy dispersive spectroscopy (EDS) analysis is conducted. Color and microstructure analysis is executed through bare-eye, macro camera, UV-VIS-NIR-colormeter, and optical microscope. The melting point, wetting angle, and hardness are measured using TGA-DTA, a wetting angle tester, and a Vickers hardness tester. The EDS analysis result demonstrates that each of the green gold alloys was manufactured with purposed contents. The color analysis result shows that the color of the alloys is similar to the color of the conventional 4 wt%- Cd 18K green gold, and the green color improves as the In content increases. The micro structure analysis result demonstrates that grain refinement improves as the amount of In increases. Enhancements in the melting point, wettability, and Vickers hardness changes appear as the In content increases and Au content decreases. The hardness is up to 260, which implies good durability. Therefore, the results suggest that the proposed 18, 14, and 8K In-added green gold alloys enhance the properties of jewelry products with regard to the green color, castability, and durability.

The properties of 18 K red gold solder alloys were investigated by changing the content of In up to 10.0 wt% in order to replace the hazardous Cd element. Cupellation and energy dispersive X-ray spectroscopy (EDS) were used to check the composition of each alloy, and FE-SEM and UV-VIS-NIR-Colormeter were employed for microstructure and color characterization. The melting temperature, hardness, and wetting angle of the samples were determined by TGA-DTA, the Vickers hardness tester, and the Wetting angle tester. The cupellation result confirmed that all the samples had 18K above 75.0wt%-Au. EDS results showed that Cu and In elements were alloyed with the intended composition without segregation. The microstructure results showed that the amount of In increased, and the grain size became smaller. The color analysis revealed that the proposed solders up to 10.0 wt% In showed a color similar to the reference 18 K substrate like the 10.0 wt% Cd solder with a color difference of less than 7.50. TGA-DTA results confirmed that when more than 5.0 wt% of In was added, the melting temperature decreased enough for the soldering process. The Vickers hardness result revealed that more than 5.0 wt% In solder alloys had greater hardness than 10.0 wt% Cd solder, which suggested that it was more favorable in making a wire type solder. Moreover, all the In solders showed a lower wetting angle than the 10.0 wt% Cd solder. Our results suggested that the In alloyed 18 K red gold solders might replace the conventional 10.0 wt% Cd solder with appropriate properties for red gold jewelry soldering.

Using a customized diffusion bonder, we executed diffusion bonding for ring shaped white gold and red gold samples (inner, outer diameter, and thickness were 15.7, 18.7, and 3.0 mm, respectively) at a temperature of 780 °C and applied pressure of 2300 N in a vacuum of 5 × 10−2 torr for 180 seconds. Optical microscopy, field emission scanning electron microscopy (FE-SEM), and energy-dispersive X-ray spectroscopy (EDS) were used to investigate the microstructure and compositional changes. The mechanical properties were confirmed by Vickers hardness and shear strength tests. Optical microscopy and FE-SEM confirmed the uniform bonding interface, which was without defects such as micro pores. EDS mapping analysis confirmed that each gold alloy was 14K with the intended composition; Ni and Cu was included as coloring metals in the white and red gold alloys, respectively. The effective diffusion coefficient was estimated based on EDS line scanning. Individual values of Ni and Cu were 5.0 × 10−8 cm2/s and 8.9 × 10−8 cm2/s, respectively. These values were as large as those of the melting points due to the accelerated diffusion in this customized diffusion bonder. Vickers hardness results showed that the hardness values of white gold and red gold were 127.83 and 103.04, respectively, due to solid solution strengthening. In addition, the value at the interface indicated no formation of intermetallic compound around the bonding interface. From the shear strength test, the sample was found not to be destroyed at up to 100,000 gf due to the high bonding strength. Therefore, these results confirm the successful diffusion bonding of 14K white-red golds with a diffusion bonder at a low temperature of 780 °C and a short processing time of 180 seconds.

In order to replace 14K white gold alloys, the properties of 5K white gold alloys (Au20-Ag80) were investigated by changing the contents of In (0.0-10.0 wt%). Energy dispersive X-ray spectroscopy (EDS) was used to determine the precise content of alloys. Properties of the alloys such as hardness, melting point, color difference, and corrosion resistance were determined using Vickers Hardness test, TGA-DTA, UV-VIS-NIR-colorimetry, and salt-spray tests, respectively. Wetting angle analysis was performed to determine the wettability of the alloys on plaster. The results of the EDS analysis confirmed that the Au-Ag-In alloys had been fabricated with the intended composition. The results of the Vickers hardness test revealed that each Au-Ag-In alloy had higher mechanical hardness than that of 14K white gold. TGA-DTA analysis showed that the melting point decreased with an increase in the In content. In particular, the alloy containing 10.0 wt% In showed a lower melting temperature (> 70 °C) than the other alloys, which implied that alloys containing 10.0 wt% In can be used as soldering materials for Au-Ag-In alloys. Color difference analysis also revealed that all the Au-Ag-In alloys showed a color difference of less than 6.51 with respect to 14K white gold, which implied a white metallic color. A 72-h salt-spray test confirmed that the Au-Ag- In alloys showed better corrosion resistance than 14K white gold alloys. All Au-Ag-In alloys showed wetting angle similar to that of 14K white gold alloys. It was observed that the 10.0 wt% In alloy had a very small wetting angle, further confirming it as a good soldering material for white metals. Our results show that white 5K Au-Ag-In alloys with appropriate properties might be successful substitutes for 14K white gold alloys.

To alloy high melting point elements such as boron, ruthenium, and iridium with copper, heat treatment was performed using metal oxides of B2O3, RuO2, and IrO2 at the temperature of 1200 oC in vacuum for 30 minutes. The microstructure analysis of the alloyed sample was confirmed using an optical microscope and FE-SEM. Hardness and trace element analyses were performed using Vickers hardness and WD-XRF, respectively. Diffusion profile analysis was performed using D-SIMS. From the microstructure analysis results, crystal grains were found to have formed with sizes of 2.97 mm. For the copper alloys formed using metal oxides of B2O3, RuO2, and IrO2 the sizes of the crystal grains were 1.24, 1.77, and 2.23 mm, respectively, while these sizes were smaller than pure copper. From the Vickers hardness results, the hardness of the Ir-copper alloy was found to have increased by a maximum of 2.2 times compared to pure copper. From the trace element analysis, the copper alloy was fabricated with the expected composition. From the diffusion profile analysis results, it can be seen that 0.059 wt%, 0.030 wt%, and 0.114 wt% of B, Ru, and Ir, respectively, were alloyed in the copper, and it led to change the hardness. Therefore, we verified that alloying of high melting point elements is possible at the low temperature of 1200 oC.

We prepared 8 samples of non-silver and silver-added master alloys containing silicon to confirm the existence of nickel-silicides. We then prepared products made of 14K and 18K white gold by using the prepared master alloys containing 0.25, 0.35, and 0.50 wt% silicon to check for nickel release. We then employed the EN 1811 testing standard to investigate the nickel release of the white gold products, and we also confirmed the color of the white gold products with an UV-VISNIR- color meter. We observed NiSix residue in all master alloys containing more than 0.50 wt% Si with EDS-nitric acid etching. For the white gold products, we could not confirm the existence of NiSix through XRD after aqua regia etching. In the EN 1811 test, only the white gold products with 0.25 wt% silicon master alloys successfully passed the nickel release regulations. Moreover, we confirmed that our white gold products showed excellent Lab indices as compared to those of commercial white gold ones, and the silver-added master alloys offered a larger L index. Our results indicate that employing 0.25 wt% silicon master alloys might be suitable for white gold products without nickel-silicide defects and nickel release problems.

Background : Yellowhorn (Xanthoceras sorbifolium Bunge) is distributed in northeastern region in China. The seeds are oil-rich and used as an edible and/or medicinal additives in China. We investigated genetic indices and molecular variance using ISSR markers and oil contents variance by analyzing fatty acid composition in several artificial populations in China. Methods and Results : Seeds were collected from four discontiguous artificial populations in four area in China : two in Inner Mongolia (IM), one in Liaoning (LN) and one in Shandong (SD). Farm in SD showed the highest number of effective alleles (Ne), Shannon index (I), and expected heterozygosity (He), i.e., 1.598, 0.470, and 0.325, respectively. Crude fat contents in kernel observed as 54.5 g 100 g-1 from SD. In contrast it was observed the lowest contents as 46.5 g 100 g-1 from LN . The fatty acid composition was determined to those of oleic acid (31.3%) from SD. And linoleic acid was determined as 38.1% from LN. These artificial populations have relatively high genetic variation, and within-population variation (23%) was higher than among populations. The artificial populations were divided into two groups, revealing these was little correlation between genetic and geographic distance. Conclusion : This study can provide the important information on genetic variation and contents characteristics. It may be responsible for the programs of improvement and germplasm conservation in the future.