In this work, a nanocomposite containing gold (Au) nanofibers decorated iron-metal–organic framework (Fe-MOF) was successfully synthesized for electrochemical detection of acetaminophen (AAP). The as-synthesized Au@Fe-MOF nanocomposite was confirmed by various characterization techniques. Morphological analysis showed that the Au nanofibers with an average size of less than 10 nm were dispersed on the Fe-MOF. Cyclic voltammetric analysis showed that the Au@Fe-MOF nanocomposite showed well-defined redox peaks with higher current than that of GCE and Fe-MOF. The Au@Fe-MOF/ GCE exhibited a linear range, sensitivity, and detection limit of 0.5–18 μM, 4.95 μM/μA/cm2, and 0.12 μM, respectively. The Au@Fe-MOF/GCE showed a very low response for the interference materials. The real sample analysis revealed that the Au@Fe-MOF/GCE showed good recovery towards the AAP in urine and paracetamol. Therefore, the developed sensor can be used for quality control of AAP.

In this report, we successfully prepared nitrogen-doped porous carbon (N-PC)/manganese dioxide ( MnO2) composite for a high-performance supercapacitor. X-ray diffraction data revealed the α-MnO2 phase. Transmission electron microscopy confirmed that the nanostructured α-MnO2 nanoparticles were coated on the surface of N-PC. The N-PC/α-MnO2 composite delivered a capacitance of 525.7 F g− 1 at the charging current of 1.0 A g− 1. The higher capacitance of the composite could be owing to the synergy of MnO2 and N-PC. Besides, the electrode exhibited a 14.7% capacitance loss after 6000 charge– discharge cycles at 10 A g− 1 indicating good electrochemical stability.

Doped porous carbon materials have attracted great interest owing to their excellent electrochemical performance toward energy storage applications. In this report, we described the synthesis of nitrogen-doped porous carbon (N-PC) via carbonization of a triazine-based covalent organic framework (COF) synthesized by Friedel–Crafts reaction. The as-synthesized COF and N-PC were confirmed by X-ray diffraction. The N-PC exhibited many merits including high surface area (711 m2 g−1), porosity, uniform pore size, and surface wettability due to the heteroatom-containing lone pair of electron. The N-PC showed a high specific capacitance of 112 F g−1 at a current density of 1.0 A g−1 and excellent cyclic stability with 10.6% capacitance loss after 5000 cycles at a current density of 2.0 A g−1. These results revealed that the COF materials are desirable for future research on energy storage devices.